简介：GaxIn1-xAs1-ySbyalloyshavebeengrownbyatmosphericpressureMOCVDonn-GaSb（Te-doped）substrate.Thesohdcompositionwasdeterminedbyusingelectronmicroprobe.ThealloysofGalnAsSbwithcompositioninmiscibilitygapweresuccessfullygrown.TheopticalpropertiesofGaxIn1-xAs1-ySbylaverswerecharacterizedbythephotoluminescenceandtheinfraredabsorption.Thespectralresponsesofp+-GaInAsSb/p-GaxIn1-xAs1-ySby/n-GaSbdetectorsshowedwavelengthcutoffat2.4μmanddetectivity-D*=5×108cmHz1/2/Watroomtemperature.

简介：LayeredcathodematerialLiCo1/3Ni1/3Mn1/3O2wassynthesizedbyPechiniprocess,andinvestigatedusingX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andgalvanostaticcharge/dischargecycling.Thesampleiswell-crystallizedandhasaphase-purea-NaFeO2structure.Theparticlesizesareuniform,anddistributedintherangeof20-200nm.TheinitialdischargecapacityoftheLi/LiCo1/3Ni1/3Mn1/3O2cellwasabout149mAh·g-1whenitwascycledatavoltagerangeof4.5-2.3Vwithaspecificcurrentof0.25mA.Theresultisbetterincomparisonwithsolid-statesolutionmethod.Thesyntheticprocedurewasdiscussed.Threemajorreactions:chelation,esterification,andpolymerizationsuccessivelyoccurred.

简介：双面挠性覆铜板及其制作方法／CN101420820／申请人广东生益科技股份有限公司本发明涉及一种双面挠性覆铜板及其制作方法，该双面挠性覆铜板包括一单面覆铜板、涂布于该单面覆铜板上的胶粘剂层、以及压覆于该胶粘剂层上的另一铜箔或另一单面挠性覆铜板，所述单面覆铜板包括一铜箔以及涂布于铜箔上的聚酰亚胺层，所述聚酰亚胺层与胶粘剂层相邻设置。

简介：EmployingLi2CO3,NiO,Co3O4,andMnCO3powdersasstartingmaterials,Li[Ni1/3Co1/3Mn1/3]O2wassynthesizedbysolid-statereactionmethod.Variousgrindingaidswereappliedduringmillinginordertooptimizethesynthesisprocess.Aftersuccessiveheattreatmentsat650and950℃,thepreparedpowderswerecharacterizedbyX-raydiffraction(XRD)analysis,scanningelectronmicroscopy,andtransmissionelectronmicroscopy.Thepowderspreparedbyaddingsalt(NaCl)asgrindingaidexhibitaclearR3mlayerstructure.ThepowdersbyothergrindingaidslikeheptaneshowsomeimpuritypeaksintheXRDpattern.Theformerpowdersshowauniformparticlesizedistributionoflessthan1μmaveragesizewhilethelattershowsawidedistributionrangingfrom1to10μm.EnergydispersiveX-ray(EDX)analysissshowthattheratioofNi,Co,andMncontentinthepowderisapproximately1/3,1/3,and1/3,respecively.TheEDXdataindicatenoincorporationofsodiumorchlorineintothepowders.Charge-dischargetestsgaveaninitialdischargecapacityof160mAh·g-1forthepowderswithNaCladditionwhile70mAh·g-1forthepowderswithheptane.

简介：前言：环境中的铅作为一种污染物，对人身体有重大危害，在全世界范围内不存在争议。现在ROHS法案即将正式实施，这标志着无铅化时代已经来临。日本是世界工业强国，为了提高竞争门槛，领先于竞争对手，现在已经制定了无卤覆铜板标准。日本企业积极行动，在国内全部采用无卤材料来生产覆铜板。本文介绍了一种同时满足无卤阻燃和适应无铅焊接的FR-1的研制工作。

简介：PolycrystallinesamplesofLa12x(Sr12yAgy)xMnO3(y=0.0,0.2,0.4,0.6,1.0)werepreparedbythesolid-statereactionmethod.ThetemperaturestabilityofmagnetoresistanceandmagnetoresistanceenhancementinLa1-x(Sr1-yAgy)xMnO3systemwithbothunivalentandbivalentelementsdopedatAsiteandwithunchangedvalueofMn3+/Mn4+ratiowereexploredthroughthemeasurementsofX-raydiffractionpatterns,magnetiza-tion-temperature(M-T)curves,resistivity-temperature(q-T)curvesandmagnetoresistance-temperature(MR-T)curves.Theresultsareasfollows:therearetwopeaksintheq-TcurvesofthesampleswithAgdoping,oneiscausedbyresistancechangeduringtheparamagnetism-ferromagnetismtransition,andtheotherisfromboundary-dependentscatteringofconductionelectronsontheboundariesofgrains.ThepeakvalueofMRincreaseswithincreasingAgdopingcontent,anditincreasesfrom8.2%fory=0.2to29.6%fory=1.0underthemagneticfieldofB=0.8T;MRremainsaconstantof12%inthetemperaturerangeof218-168Kforthesamplewithy=1.0,andthetemperaturestabilityofMRisinfavorofthepracticalapplicationofMR.

简介：本文论述了多层挠性线路板在设计时应如何保证线路在挠曲时的可靠性。以及一些常用的设计方法。

简介：TheintermetalliccompoundZr1-xTixCowaspreparedanditssuitabilityforhydrogenstoragewasinvestigated.ThealloysobtainedbymagneticlevitationmeltingwiththecompositionofZr1-xTixCo(x=0,0.1,0.2and0.3,at.%)showsinglecubicphasebyX-raydiffraction.Asingleslopingplateauwasobservedoneachisothermal,andpressure-composition-temperature(PCT)measurementresultsshowthattheequilibriumhydrogendesorptionpressureofZr1-xTixCoalloyincreaseswithincreasingTicontent.Thedesorptiontemperaturesforsupplying100kPahydrogenareabout665,642,621and614KforZrCo,Zr0.9Ti0.1Co,Zr0.8Ti0.2CoandZr0.7Ti0.3Coalloy,respectively.RepeatedhydrogenabsorptionanddesorptioncyclesdonotgenerateseparatedZrCo,TiCoandZrH2phases,indicatingthatalloyshavegoodthermalandhydrogenstabilization.

简介：

简介：上周金价在达到1260美元上方高点后，出现小幅回调，一度跌破1230美元。有分析人士认为，增加人民币汇率弹性使得人民币兑美元创下新高，而黄金以美元计价，人民币升值对黄金短期利空。

简介：据《新物流》周刊报道,2003年伊始,华东、东北、中南等地废钢市场价格迅猛上扬。1月上中旬,江、浙、沪鲁钢厂重型废钢采购含税价每吨升至1320-1340元,中型废钢升至1280-1300元,统料废钢升至1180-1200元,与2002年末比统料升幅60-70元,重型和中型废钢上升100-120元。另据宝钢实业公司、

简介：通过等温拉伸实验研究双态组织Ti-6Al-2Zr-1Mo-1V合金的热变形行为、显微组织演变与断裂特征。结果表明:材料的流动软化由双态组织动态球化引起,并导致较高的应力指数和热激活能。结合SEM、EBSD和TEM显微组织观察发现,750和800℃下动态球化由α/α亚晶界的形成与β相的渗透共同导致;而在850℃下由于低角度晶界向高角度晶界转化,生成呈项链状分布的细小晶粒,证明该温度下主要的球化机制为动态再结晶。随着变形温度的升高或应变速率的减小,合金的断裂机制由微孔聚集向沿晶断裂转变。

简介：虽然由于应用铜箔制造企业不同，使得所生产出的电解铜箔在性能上各有特色，但制造工艺却基本一致。即以电解铜或具有与电解铜同等纯度的电线废料为原料，将其在硫酸中溶解，制成硫酸铜溶液，以金属辊筒为阴极，通过电解反应连续地在阴极表面电解沉积上金属铜，同时连续地从阴极上剥离，这工艺称为生箔电解工艺。最后从阴极上剥离的一面（光面）就是层压板或印刷线路板表面见到的一面，反面（俗称毛面）就是需要进行一系列表面处理，在印刷线路板中与树脂粘接的一面。

简介：建滔化工主席张国荣表示，覆铜板业务溢利由2010年时逾21亿元的水平，逐步降至去年仅11亿，但他料未来1～2年业务由谷底回升。

简介：一、宏观经济若干热点问题（一）全球经济二次探底的可能性2010年一季度，世界各主要经济体都出现了强劲的增长。美国公布的GDP折年率较上一季度增长了3．2％，按可比价格计算其一季度GDP同比增长了2．5％，按现行价格计算增长了3％。

简介：12009年全球线路板市场概述IPC在2010年10月出版了2009年度全球PCB市场报告。根据IPC全球市场共识委员会提供的美元数值估计,2009年全球PCB产值统计为442.2亿美元左右,

简介：ＶｅｒｔｉｃａｌＧｒａｄｉｅｎｔＦｒｅｅｚｅＧｒｏｗｔｈｏｆＣｄ＿（１－ｘ）Ｚｎ＿ｘＴｅｗｉｔｈＣｄ／ＺｎＲｅｓｅｒｖｏｉｒＨｏｕＱｉｎｇｒｕｎ；ＷａｎｇＪｉｎｙｉ；ＤｅｎｇＪｉｎｃｈｅｎｇ；ＬｉＭｅｉｙｉｎｇａｎｄＴａｏＦｅｎｇ（侯清润）（王金义）...

简介：WehavecalculatedtheelectronicstructuresofCo2FeAl1-xSix(101)surfaceusingfirst-principlesmethodbasedonthedensityfunctionaltheory.Becauseofthesurfaceeffect,theminorityspinbandgapattheFermileveldisappearsatthesurfaceofbulkCo2FeAl1-xSix.However,beneaththesurface,theminorityspingapopensattheFermilevel,whichindicatesthattheelectronicstructuresofCo2FeAl1-xSix(101)be-comeclosetothatofbulkphase.Accordingly,theCo2FeAl1-xSix(101)surfaceisacompositetri-layerstructurethatcorrespondstotheweakeningofhalf-metallicpropertyinCo2FeAl1-xSixfilms.Eventhough,thespinpolarizationofCo2FeAl1-xSix(101)surfaceisstilllargerthanthatofCo2FeAlorCo2FeSimaterials,makingCo2FeAl1-xSixapromisingspintronicsmaterial.

简介：

简介：2014年1～3月,覆铜板出口量、出口额同比都为负增长,1季度累计同比分别减少7.00%和7.15%,4月同比、环比都改变为正增长,所以1～4月累计同比虽然仍为负增长,但较一季度分别收窄3.48和2.89个百分点。2014年1～3月,覆铜板进口额每月同比都为正增长,1季度累计进口额同比增长6.81%;而进口量1、3月为负增长,2月为正增长,1季度累计进口量同比增长0.34%,