简介：ProblemsaboutsurfacemountingprocessforfinepitchdevicesandreasonsonsolderbridgingofLtypeleaddevicesweldedaredepicted.Bridgingmechanismandinfluencefactorsareanalyzedwithtwo-dimensionalgeometricmodel.Basedonthis,high-densitysurfacemounttechnology(SMT)forfinepitchLtypeleaddevicesheatedbyscan-ninglaserisraised.SurfacemountprocessforQFP208onprintedcircuitboard(PCB)isstudied.Theresultsoftestsarethatitisquitepossibletosolvethesolderbridgingofsurfacemountingforpitchdeviceswithscanninglaser-heat-ingmethod.

简介：904L是一种全奥氏体不锈钢,在焊接时易出现热裂纹,且晶间腐蚀和应力腐蚀开裂倾向较大。本文经可焊性分析后,从焊接材料和焊接工艺参数的选择入手,进行了焊接工艺性试验,找出了合适的焊接规范,并在实际产品的焊接中进行了严格的质量控制,生产出合格的产品。

简介：

简介：Intheacceleratordrivensub-criticalsystem(ADS)cooledbyliquidPbBialloy,theausteniticstainlesssteel316Lisoneofthecandidatesofstructuralmaterials.However,thecorrosionandwearbehaviorof316Lsteelinthehigh-velocitystreamofliquidPbBiisthemostessentialissue,whichisurgenttobepaidcloseattention.Inordertoacquirethemorphologyandmechanicalpropertiesof316Lsteelintheconditionsofdifferentrelativeflowingvelocity(RFV),respectively2.62m/s,3.69m/s,4.77m/s,theexperimentwascarriedoutindynamicliquidPbBiat550℃,uptoabout1500h.Accordingtotheresults,thesurfaceof316LhasbeencorrodedbadlyandtheelementsofNi,Cr,etc.werefoundtodissolvealot.WiththeincreaseoftheRFV,thefeatureof316Lsurfacechangedfromthesurfacewithmuchdeeperpitsandlooserstructurestotherelativeplanarone,andthethicknessoftheouteroxidelayerdecreasedgraduallywhilethatoftheinneroxidelayerdiminishedalittle,andthemicrohardnessoftheoutermostsubstratealsodeclinedincreasingly,inaddition,thedomainofthepartialsubstratewithitsmicrohardnessbeingaltereddeepenedfurther.Theseexperimentaldatawouldoffertheoreticalbasisandpracticalvaluestostudycorrosionconditionof316LsteelinliquidPbBiwithhigh-velocity.

简介：随着2001年第一缕曙光的到来,历史翻开了崭新的一页,一个新世纪诞生了。新世纪给我们带来了五彩斑斓的遐想,但同时也为我们带来了理智的沉思。世界经济一体化发展的必然趋势,给我国电焊机行业提出更多的是严峻的挑战。在当今日趋激烈的市场竞争、市场国际化以及价格大战中,我国电焊机制造业和产品结构应向何处发展?如何在站稳国内市场的基础上,走出国门,立于世界之林?这是新世纪初年我国电焊机行业面临的头等大事,一道与企业性命攸关的重大试题。如何应对?请恭听来自行业同仁之声,供您解题参考。

简介：<正>21世纪初期是实现中国现代化发展战略的关键时期。参与经济全球化进程中的国际经济和科技的激烈竞争,面对促进国内产业结构优化升级的艰巨任务,加快发展高技术产业是必然的选择。一、正确处理影响发展战略的重大关系1.引进技术与自主创新的关系近年来,依靠国外直接投资或合资建设发展起来的电子,移动通信设备制造等产业,迅速缩短了中国与国外先进技术的差距。引进技术对加快中国高技术

简介：

简介：BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope（SEM）,electron.probemicroanalysis（EPMA）andX-raydiffraction（XRD）.theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.

简介：本文结合生产实践,简要分析提出了CO2气体保护焊目前所存在的缺陷与问题,并提出了相应的解决方法与CO2气体保护焊的发展趋势。

简介：ＡｖｉｓｉｏｎｔｒａｃｋｉｎｇｓｙｓｔｅｍｏｆｒｏｂｏｔＣＯ２ｓｈｏｒｔｔｒａｎｓｆｅｒｗｅｌｄｉｎｇＷｕＲｅｎｙｕ；ＷａｎｇＧｕｏｄｏｎｇａｎｄＬｉＸｉａｏｑｉ（ＴｉａｎｊｉｎＵｎｉｖｅｒｓｉｔｙ）ＺｈａｎｇＬｉａｎｃｈａｎｇ(ＭｏｔｏｒｏｌａＣ?..

简介：

简介：本文介绍了CO2气体保护电弧焊的冶金特点，CO2气体保护电弧焊焊接过程中的熔滴过渡形式；从焊丝的冶金过程，焊接时的工艺参数的选择及调整等方面探讨了汽车白车身CO2焊接质量的控制。

简介：IntheautomaticCO2arcwelding,thealterationoftheverticaldistancebetweentheweldingtorchandtheworkpiecehasastrongeffectontheweldingparameterssuchasweldingcurrentandvoltage,withtheresultthattheappearanceandqualityofweldarenotsteady.Toweakentheinfluenceofthedistancealteration,amethodisputforwardinthepaper.Themethodisthatthealternatewire-feedcontrolisusedforcompensatingtheweldingcurrent.Onthebasisoftheoreticalanalysis,astaticnumericalmodelforalternatewire-feedcontrolisestablished.Theexperimentsshowthatthemodel-basedregulationofthewirefeedratecancompensatetheweldingcurrentandensuretheappearanceofweld.Whenthealterationofverticaldistancebetweenthetorchandtheworkpieceisgreater,notonlyisthewirefeedrateregulated,buttheoutputvoltageofthepowersourceisadjustedtoensuretheappearanceandqualityofweld.

简介：本文介绍了CO2焊工艺方法及其高效、优质、低成本的综合优越性以及在石油、化工、天然气工程建设中的应用与发展,不同种类的气体与焊丝相组合的工艺特点及控制焊缝成形的操作技术。

简介：

简介：<正>21世纪的第一个年头,西部大开发拉开了序幕,给我国焊接行业带来了新的发展机会和好的兆头。中国焊接博览会"西部焊接论坛"正是在这个时机,在蔚为大观的第15届中国焊接博览会期间——5月18日在成都国际会展中心召开了。这次"论坛"目的在于,探讨焊接行业在我国西部大开发中的作用与发展机遇。大会组委会应行业的要求,借焊博会在西部举办之机,邀请焊接行业及西部最具代表的焊接大户聚在一起、共商焊接行业在西部大开发中的作为,探讨焊接行业如何满足西部

简介：

简介：ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.

简介：针对某企业支架制造过程中采用二氧化碳气体保护焊，焊接接头出现大量未熔合缺陷，分析了未熔合产生的原因，并阐述了防止未熔合的措施。实践证明该措施有效地控制了未熔合缺陷，提高了焊缝合格率，获得了满意的焊缝质量，具有推广应用价值。同时，是否将“未熔合”焊接缺陷与“气孔和飞溅”相提并论，都是CO2焊时容易出现的缺陷，以引起同仁的重视。

简介：AnewkindofsimpleandflexibleCO_2weldingsystemwasdevelopedtocarryoutwaveformcontrol.ThesystemconsistedofIGBTinverter,PWMcircuitandmicroprocessorunit(MPU),inwhichtheoutputcurrentofconstantcurrent(CC)powersupplycouldbechangedaccordingtotransientphysicalstate,andthevariabledownsloperatecontrolcouldbeusedtoensureastableweldingprocess.Theweldingexperimentresultsprovedtheeffectivenessofthiscontrolapproach.