简介：评价了具有不同Ni/(Ni+W）原子比的NiW/γ－Al2O3催化剂加氢脱硫活性，对硫化态催化剂进行了EXAFS表征。结果表明，Ni(Ni+W)原子比为0．23的催化剂表面上WS2颗粒最小，有利于形成Ni-W-S加氢脱硫活性相，其反应活性最高。

简介：UnipolarresistiveswitchingbehaviorsoftheZnOandAl2O3/ZnOfilmsfabricatedonflexiblesubstratesbypulselaserdepositionwerestudiedinthispaper.Thefilmsweredepositedatroomtemperaturewithoutpost-annealingtreatmentduringtheprocess.XraydiffractionresultsindicatedthatZnOfilmhasadominantpeakat(002).ScanningelectronmicroscopyobservationshowedacolumnargrainstructureoftheZnOfilmtothesubstrate.ThebilayerdeviceofAl2O3/ZnOfilmshadstableresistiveswitchingbehaviorswithagoodenduranceperformanceofmorethan200cycles,highresistiveswitchingratioofover103atareadvoltageof0.1V,whichisbetterthanthatofthesingleoxidelayerdeviceofZnOfilm.Apossibleresistiveswitchingfilamentarymodewasdemonstratedinthispaper.TheconductionmechanismsofhighandlowresistancestatescanbeexplainedbyspacechargelimitedconductionandOhmic’sbehaviors.Theenduranceofthebilayer(BL)devicewasnotdegradeduponbendingcycles,whichindicatesthepotentialoftheflexibleresistiveswitchingrandomaccessmemoryapplications.

简介：对固溶–淬火处理后的Al-3.7Cu-1.6Mg合金板材进行变形量分别为0、5%和10%的预拉伸处理,然后置于空气中进行自然时效,研究预变形对Al-3.7Cu-1.6Mg合金自然时效态的硬度、室温拉伸性能和断裂韧性的影响,利用扫描电镜（SEM）与透射电镜（TEM）观察合金的显微组织及断口形貌,研究其断裂机理。结果表明：该合金在淬火后引入预拉伸变形,可显著提高其自然时效态的硬度和屈服强度,同时抑制GPB区的形成,降低时效析出速率,并使峰时效时间延长;随预变形量从0增加至10%,Al-3.7Cu-1.6Mg合金的断裂韧性降低,这主要是预变形增加了基体内的位错密度,位错切割细小的GPB区粒子,大量滑移被抵消,造成变形过程中局部应力集中,从而形成微裂纹;由断口分析可知该合金的断裂类型为穿晶韧窝型断裂,且随预变形程度增大,韧窝直径和深度均增大。

简介：

简介：TheatomicscalecomputersimulationforinitialprecipitationmechanismofNi75Al6V19alloywascarriedoutforthefirsttimebyemployingthemicroscopicdiffusionequation.Theinitialprecipitationprocesswasinvestigatedthroughsimulatingtheatomicpicturesandcalculatingtheorderparametersofthetwokindsoforderedphases.Simulationresultsshowthattheγ′orderedphaseprecipitatedearlierthanθorderedphasebycongruentordering+spinodaldecompositionmechanismandthusproducedanonstoicheometricγ′singleorderedphase.Then,thenonstoichiometricθphaseprecipitatedbyanon-classicalnucleationandgrowthmechanismattheAPBSofγ′phase.

简介：分析了影响45Mn17Al3钢磁导率性能的主要因素。通过工业试验确定了合理的化学成分、热处理工艺制度及试样表面加工要求等。试验结果表明,45Mn17Al3钢在800、4000及8000A/m三个磁场强度下,相对磁导率μr≤1.005,满足了某些特殊工程对磁性能的较高要求。

简介：Theglass-formingability(GFA)andmagneticpropertiesoftheGd_(50)Coso-basedamorphousaiioywithAladditionsubstitutionforCoareinvestigated.ItisfoundthattheGFAandmagneto-caloriceffectoftheGd_(50)Co_(45)Al_5amorphousaiioyarebetterthanGd_(50)Co_(50)amorphousalloy.Themaximummagneticentropychange(-△S_m~(peak))andthemagneticrefrigerantcapacityoftheamorphousalloyunderafieldof5Tareabout6.64J·kg~(-1)K~(-1)and764J·kg~(-1),respectively.Thefielddependenceofmagneticentropychangemeetstheonepredictedbythemeanfieldtheory,whichisinvestigatedforabetterunderstandingofthemagneto-caloricbehaviorsoftheGd_(50)Co_(45)Al_5amorphousalloy.

简介：Opticalmicroscope（OM）,scanningelectronmicroscope（SEM）,energydispersivespectrometer（EDS）andX-rayDiffraction（XRD）wereusedtostudytheeffectsofrareearthonthemicrostructuralcharacteristicsof55%Al-Zn-1.6%Sihot-dipcoatingsonsteel.TheresultsofOM,SEMandEDSshowedthatbyaddingREintothe55%Al-Zn-1.6%Sibath,thesaw-toothedshapeofintermetallicreactionlayerofcoatingbecamesmooth,andthethicknessoftheoverlayandintermetallicreactionlayerdecreased.TheXRDresultsrevealedthattheintermetallicreactionlayerwascomprisedoftwodifferentregions,abrightphaseclosesttothesteelsubstratewithphasesofFe2Al3andadarkphaseclosesttothemetalliccoatingwithphasesofFeAl3/α-Fe-Al-Si.

简介：摘要本文通过实验室试验研究了Al、N元素对Q345E钢性能的影响。结果表明，适量添加Al元素并严格控制N元素含量可有效改善Q345E钢的低温冲击韧性。

简介：摘要：对CRH380AL动车组直流电源系统工作原理、特点进行分析，结合其特性并根据运用中的问题提出想法，对实际检修工作进行理论探讨。

简介：在二种铝锂alloys2090和2090+Ce的脱臼的微观结构借助于TEM技术被观察。到力量的8''和T_1precipitates的贡献被使用量的金属组织学的结果和微变丑的行为的分析独立计算；三角洲的共同加强的效果“andT_1猛抛被学习。结果证明三角洲共同加强的增加的关系“并且T_1根据1.4以近的山峰条件形成的q=，即，三角洲tau_p~(1.4)=三角洲字形物_(三角洲“)~(1.4)+三角洲字形物_(T_1)~(1.4)；但是增加的关系是近似一种线性关系(q=1)以未成年的条件并且成为抛物线形式什么时候over-aged(q=2)。共同加强的增加的关系三角洲的贡献“并且显然依赖于老化时间的T_1is。

简介：摘 要：氧化铝陶瓷因其优异性能被广泛应用，而脆性严重限制其使用场景。碳化硅晶须有着与氧化铝相似的热膨胀系数，且与氧化铝物理、化学性质相匹配，这使SiCw增强Al2O3陶瓷成为可能，本文将简述SiCw/Al2O3陶瓷制备。

简介：β-phase上的超声的处理的效果(Mg17Mg-9.0wt.%Al合金的艾尔12)形态学被学习。结果证明与在Mg-9.0wt.%Al团结期间采用的高紧张的超声的颤动，在营舍的全部生气的节的β-phase显著地被精制并且也变化了从对不连续的形态学连续。球形的β-phase在与高紧张的超声的颤动对待的营舍的团结期间被形成。

简介：摘要：铝是钢铁的常用金属，具有易导电、密度小、易延展、耐腐蚀等优点，在我国国民经济中占有重要地位。如果在铝电解槽中加入氧化铝的同时, 加入钛的氧化物或化合物，在不改变电解作业规程的条件下，生产出化学成分、金相组织以及细化效果均理想的铝钛合金，就能达到简化生产工艺，减少能耗，降低成本，提高细化剂质量的目的。

简介：摘要：

简介：摘要： 时速300公里以上的动车组，无论是在车身重量还是车体强度上，都有着严格的要求。以7N01系铝合金为代表的Al-Zn-Mg高强铝合金因其优异的性能，被广泛应用于铁路、航空等特种设备上。铝合金强度越高，时效强化相含量随之升高，同时强化相在晶界富集，晶界断裂成为断裂的主导因素，最终导致合金的断裂韧性和应力腐蚀抗性降低。本文通过高温压缩试验，分析研究动车组高强铝合金车体的热力学性能，分析热处理工艺对其组织和性能的影响，优化热加工过程中的工艺参数，进而指导实际生产。

简介：摘要：本文通过利用氧化铝掺杂氧化锌组成ZnO−Al2O3二元体系，研究氧化铝对氧化锌陶瓷电阻的致密度、晶相、微观形貌及电阻率的影响。Al2O3加入ZnO中，Al2O3优先与ZnO固溶，生成固溶体；随Al2O3含量的增多，ZnO陶瓷的致密度先提高后逐渐降低，1mol% Al2O3含量的致密度最高；Al2O3含量为0.5 mol%的瓷体由于气孔较多，致密度低；随Al2O3掺入量的增加，当生成第二相ZnAl2O4时，形成受主能级和空位补偿，使电阻率提高，平均值由掺杂1mol% Al2O3时的5.2Ω·mm上升到掺杂4mol% Al2O3时的15.7Ω·mm。

简介：Ahighlyreliableinterfaceofself-alignedbarrierCuSiNthinlayerbetweentheCufilmandthenano-porousSiC:H(p-SiC:H)cappingbarrier(k=3.3)hasbeendevelopedinthepresentwork.Withtheintroductionofself-alignedbarrier(SAB)CuSiNbetweenaCufilmandap-SiC:Hcappingbarrier,theinterfacialthermalstabilityandtheadhesionoftheCu/p-SiC:Hfilmareconsiderablyenhanced.AsignificantimprovementofadhesionstrengthandthermalstabilityofCu/p-SiC:H/SiOC:Hfilmstackhasbeenachievedbyoptimizingthepre-cleanstepbeforecap-layerdepositionandbyformingtheCuSiN-likephase.ThiscaplayeronthesurfaceoftheCucanprovideamorecohesiveinterfaceandeffectivelysuppressCuatommigrationaswell.

简介：摘要：探讨了电力系统自动化技术在Al-Cu-Mg合金耐蚀性能调控中的应用及其面临的技术集成难度、耐蚀性能评估标准、经济性与可行性等关键问题，一是分析了技术集成过程中存在的多学科交叉复杂性及系统间兼容性问题，强调了加强技术集成与创新的重要性。二是针对耐蚀性能评估标准的缺失，提出了完善评估体系的建议，包括制定统一测试方法、建立多维度评估指标等。最后从经济性与可行性角度出发，讨论了降低成本、优化效益、对接市场需求及加强国际合作等策略。旨在为Al-Cu-Mg合金在电力运输系统中的广泛应用提供理论支持与实践指导。

简介：