简介：

简介：采用回流沉淀法、微波模板辅助法和水热法分别制备了TiO2纳米颗粒，采用Xrd对催化荆进行了表征。考察了不同制备方法的催化剂光催化活性。实验结果表明，3种方法制备的TiO2对甲基橙溶液的光催化降解能力较高，采用微波模板辅助法制备的TiO2催化剂催化活性最高，对甲基橙的降解效果最好。催化剂用量为0．4g，紫外光照射60min，浓度为12mg／L的甲基橙溶液降解率为80％。

简介：

简介：摘要  本文分析TiO2对烧结利用系数、转鼓强度以及冶金性能的影响，采取提高SiO2/TiO2比值、提高料层厚度和配碳量、配加氧化锰、氧化硼、萤石等措施，改善烧结矿质量和利于高炉稳定顺行。

简介：ItiswellknownthatthephotocatalyticactivityofTiO2thinfilmsstronglydependsonthepreparingmethodsandpost-treatmentconditions,sincetheyhaveadecisiveinfluenceonthechemicalandphysicalpropertiesofTiO2thinfilms.Therefore,itisnecessarytoelucidatetheinfluenceofthepreparationprocessandpost-treatmentconditionsonthephotocatalyticactivityandsurfacemicrostructuresofthefilms.ThisreviewdealswiththepreparationofTiO2thinfilmphotocatalystsbywet-chemicalmethods(suchassol-gel,reversemicellarandliquidphasedeposition)andthecomparisonofvariouspreparationmethodsaswellastheiradvantageanddisadvantage.Furthermore,itisdiscussedthattheadvancementofphotocatalyticactivity,super-hydrophilicityandbactericidalactivityofTiO2thinfilmphotocatalystinrecentyears.

简介：根据烧结矿强度现状,从原料结构、工艺因素、流程等方面进行分析,并提出改进措施,以减少5～10mm入炉烧结矿粒级,改善粒度组成。

简介：摘要：

简介：TiO2/Au/TiO2多层的薄电影用dc(直接水流)在房间温度在聚合物底层被扔磁控管劈啪作响方法。由改变每层的厚度，TiO2/Au/TiO2多层的电影的光、电的性质能被定制适合不同应用。厚度和Au层的光性质和Au绝缘的接口的质量为Au绝缘的多层的薄电影的电、光的表演是批评的。在8nm的厚度，Au层形成有最低抵抗力和它的连续结构一定为高发射度薄。多层的栈能被优化有6的一个表电阻?在在在波长的680nm的超过80%的发射度的/sq.。当时，山峰发射度向长波长区域变二TiO2的厚度(上面、更低)层增加。当二部TiO2电影的电影厚度是45nm时，高发射度价值为全部可见轻波长区域被获得。

简介：TiO_2isapromisingphotocatalyst.However,thelowphotocatalyticefficiencycallsforthemodificationofTiO_2.Metal-andnonmetal-dopingofTiO_2havebeenprovedtobeeffectivewaystoenhancephotocatalyticproperties.Thisreviewprovidesadeepinsightintotheunderstandingofthemetal-andnonmetal-dopedTiO_2photocatalysts.ThisarticlebeginswiththeintroductionofthecrystalstructuresofTiO_2andapplicationsofTiO_2materials.Wethenreviewedthedoped-TiO_2systemintwocategories:(1)metal-dopedTiO_2photocatalystssystem,and(2)nonmetal-dopedTiO_2photocatalystssystem.Bothexperimentalresultsandtheoreticalanalysesareelaboratedinthissection.Inthefollowingpart,fortheadvantagesofTiO_2thinfilmsoverparticles,variouspreparationmethodstoobtainTiO_2thinfilmsarebrieflydiscussed.Finally,thisreviewendswithaconciseconclusionandoutlookofnewtrendsinthedevelopmentofTiO_2-basedphotocatalysts.

简介：

简介：在酸性TiO2水悬浮体系中，利用光催化反应生成的羟基自由基可以实现对于VX的有效消毒。VX降解历程主要是通过P-S键的断裂，生成低毒或无毒的中间产物，甲基膦酸二乙酯、甲基膦酸等。随着反应的继续，最终达到彻底矿化，最终产物为SO4^2-、NO3^-、PO4^3-和CO2。生成的SO4^2-离子浓度与反应中硫元素彻底矿化的量相对应，而反应生成的NO3^-、PO4^3-远小于其理论矿化值，这表明在酸性条件下光催化消除VX是一个有选择的过程。

简介：HuntsmanTioxide公司自2004年10月1日以来将所有的二氧化钛产品价格上调，出售给全球用户。在美国，除FC5，TR28和所有锐钛型产品上涨0．07美元／lb外，其它所有产品均上涨O．06美元／lb。在加拿大，FC5、TR28和所有锐钛型上涨0．09加元／lb，其它所有产品上涨0．08加元／lb。在欧洲，

简介：TheinfluenceofcalcinationtemperatureonTiO2nanotubes’catalysisforTiO2/UV/O3wasinvestigated.TiO2nanotubes(TNTs)werepreparedviathesol-gelmethodandcalcinedat300—700℃,whichwerelabeledasTNTs-300,TNTs-400,TNTs-500,TNTs-600andTNTs-700,respectively.TNTswerecharacterizedbytransmissionelectronmicroscopy(TEM)andX-raydiffraction(XRD).ItisfoundthatTNTscalcinedat400℃showedthebestthermalstability.Whenthecalcinationtemperatureincreasedfrom400℃to700℃,thespecialstructureoftubeswasdestroyedandgraduallyconvertedintonanorodsand/orparticles.Thetransformationfromanatasetorutileoccurredat600℃,andtherutilephasewasenhancedwhenthecalcinationtemperaturewasincreasedtoover600℃.Thecalcinationtemperature’sinfluenceonTNTs’adsorptionactivityforchemicaloxygendemand(COD)andcatalyticactivityforTiO2/UV/O3wasinvestigatedinlandfillleachatesolution.Inlandfillleachatesolution,theadsorptionactivityofCODdecreasedinthereducedorderofTNTs-300,TNTs-400,TNTs-500,TNTs-600andTNTs-700.Inphotocatalyticozonation,TNTs-400showedthebestcatalyticactivitywhileTNTs-700exhibitedtheworst.Inotherthreeprocesses,theCODremovalofTNTs-300/UV/O3washigherthanthoseofTNTs-500/UV/O3andTNTs-600/UV/O3inthefirst20min,andthenbecameclosetothoseofthelattertwointhefollowing40min.ComparedwithTNTs-300andTNTs-400,TNTs-600hadthebestanti-foulingactivity,whileTNTs-500andTNTs-700hadloweranti-foulingactivitythantheformerthree.Inphotocatalyticozonation,thecalcinationtemperatureof400℃wasappropriatewhenTNTswereobtainedatthesynthesistemperatureof105℃.

简介：摘要采用光学显微镜及ＩＰＰ软件对高碱度烧结矿显微结构及矿物组成进行了研究，并检测和分析了高碱度烧结矿的冶金性能。研究结果表明高碱度烧结矿主要由赤铁矿、磁铁矿、铁酸钙、硅酸二钙等矿物组成，不同碱度条件的烧结矿显微结构基本相似，主要为交织熔蚀结构；当碱度从１．５提高到２．０时，烧结矿中的赤铁矿质量分数增加了８％，磁铁矿质量分数降低了１８％，铁酸钙质量分数增加了２３％，磁铁矿与铁酸钙形成熔蚀结构；烧结矿的成品率从７５．０９％增加到８２．７８％之后稍有降低，转鼓指数从５４％增加到６９．３３％，低温还原粉化性能和还原性均得到较大改善。

简介：摘要：为确保高炉低硅烧结矿的顺利稳定融合，研究了二氧化硅含量降低对烧结和综合炉料冶金性能的影响，并优化了低硅烧结矿在烧结成分方面的冶金性能，结果表明，当二氧化硅含量从5 %下降到4.8%时，烧结矿的RDI变化不大；尽管二氧化硅含量继续下降，但由于氯化钙的注入，可大大降低二氧化硅含量。RI在低硅烧结的生产和应用中不是一个有限的环节。二氧化硅含量下降到4.8%的两组烧结矿具有最佳的软化特性，随着二氧化硅含量的持续下降，烧结矿的熔炼间隔略有扩大。矿用烧结、水煤炉结构优化后，高炉合料的冶炼性能显着提高。

简介：初步探讨了以Yb2O3／TiO2鼓泡空化降解有机染料，研究了鼓泡时间、染料初始浓度、催化剂含量、气体流速对刚果红降解率的影响，对比了不同染料的降解率及可能的降解过程。

简介：摘要：本研究旨在探讨烧结矿中MgO含量对烧结矿强度的影响。首先，分析了烧结矿中MgO含量的影响因素，包括原料中MgO的含量、烧结工艺对MgO含量的影响以及烧结矿中MgO含量的检测方法。随后，详细研究了MgO含量与烧结矿强度之间的关系，以及MgO含量对烧结矿物理性能和冶金性能的影响。通过实验研究，发现适量的MgO含量可以显著提高烧结矿的强度，改善其物理性能，并对冶金性能产生积极影响。本研究为优化烧结矿生产工艺、提高烧结矿质量提供了重要的理论依据和实践指导。

简介：采用在位高压Raman光谱和高压同步辐射能散X射线衍射技术，在室温下对晶粒尺寸为10nm的锐钛矿TiO2进行了压致相变研究，压力范围分别为42．9GPa和23．0GPa，实验结果表明，在16．3GPaTiO2发生了一次结构相变，由原来的锐钛矿结构变为α－PbO2结构（TiO2-Ⅱ），该相变是不可逆的。同体材料TiO2的高压相变结果比较，由于晶粒尺寸的效应，纳米尺寸的锐钛矿TiO2的相变压力明显高于体材料的相变压力。

简介：ThephotodegradationreactionrateofCHCl3inTiO2particulatesuspensionwasimperovedsignificantlybyHCl-treatment.TheeffectofHCl-treatmentonthephotocatalyticactivityofTiO2wasstrdiedinaPECcellbyusingIntensity-ModulatedPhotocurrentSpectroscopy(IMPS).ThemagntudeofphotocurrentresponseandthecharacteristicfrequenciesoftheupperandlowersemicirclesinthecomplexplaneofIMPSresponsewereanalyzed,andtheccathodicandanodicreactionprocessesofphotogeneratedholesandelectronswerediscussed.Theincreasesinthecathodicandanodicphotocurrentresponseandinthetimeconstantsofbothcathodicandanodicreactionprocessesofphotogeneratedholesandelectronswerediscussed.TheincreasesinthecathodicandanodicphotocurrentresponseandinthetimeconstantsofbothcathodicandanodicreactionprocessesindicatethatHCl-treatmentleadstotheimprovementofthephotocatalyticactivityofTiO2andachangeofthephotocatalytickineticmechanism.

简介：HomogeneousNi2+-dopedtitaniagelwassynthesizedbyasol-gelprocess,andthexerogelwasthenobtainedthroughaginganddrying,leadingtotheformationofNi/TiO2nanocompositeafterheattreatmentunderasuitablereducingatmosphere.TheresultingnanocompositewascharacterizedbyTGA-DSC,TEM,XRDandBETmethods.Theresultsshowthatthestructureandgrainsizeofthenanocompositescouldbemanipulatedbyalteringtheheat-treatmentconditions,andthatthenanocompositepossessesamesoporousstructurewithaporeradiusofca.28nmandaspecifictheanatase-rutilephasetransformation.