简介：本文针对N4／1Cr18Ni9Ti与N4／0Cr25Ni20复合板的特殊焊接要求，根据NB／T47014—2011《承压设备焊接工艺评定》的要求，制备2块N4／1Cr18Ni9Ti试板，2块N4I／0Cr25Ni20试板，尺寸均为500mmX150mmX（4＋14）mm。不锈钢基层采用GTAW打底，焊丝选用HOCr21Ni10，SMAW填充与盖面，焊条选用A302与A402。镍复层的焊接采用手工钨极氩弧焊，焊丝选用含Ti、AI等脱氧元素的ERNi-1焊丝，保护气体选择98％Ar＋2％H2。试板焊接完成，外观检验合格后进行100％RT，检测结果符合JB厂r4730，2—2005I级合格，镍复层进行100％PT，检测结果符合JB／T4730．5—2005I级。两种焊接试板分别取样并做拉伸、弯曲力学性能分析，镍复层焊缝做化学成分分析。通过两块焊接试板试验对比，不锈钢基层焊接材料选择HOCr21Ni10焊丝与A302焊条。镍复层焊接采用ERNi-1焊丝，焊接保护气体为98％Ar＋2％H2。通过焊接工艺评定试验研究，解决了N4／1Cr18Ni9Ti与N4I／0Cr25Ni20复合板焊接问题，提高了用户坩埚的返修质量与再次使用寿命，为使用单位节约了成本。

简介：分别采用低强匹配焊丝ER50-6、等强匹配焊丝ER-60G和超强匹配焊丝ER-70G，对高强度钢610L进行焊接，对比三种焊接试样的机械性能、抗裂性以及金相组织，验证焊材的匹配性。

简介：Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.

简介：WeldingresearchofA6N01S-T5aluminumalloyprofileforhigh-speedtrainwasdonebyusinglaser-MIGhybridweldingandMIGweldingindividually.Andtheweldappearance,weldingdistortion,mechanicalpropertiesofthejointsandmicrostructureswereanalyzed.Thetestresultsdemonstratedthathigh-efficientweldingfortheprofilecanbeachievedbyusinglaser-MIGhybridwelding,thespeedofwhichcanbeover3.0m/min.Theprocessinghadagoodgapbridgingability，evenifthegapofthebuttjointwasupto2.0mm,agoodweldappearancecanalsobegot.Whilethehybridweldingspeedwasgreaterthan2.5m/min,theweldingdistortionofthelaser-tandemMIGhybridjointswasjustabout33%ofthatoftheMIGjoints,buttheweldingefficiencywasover3timesofMIGwelding.Andtensilestrengthofthehybridjointswas85%ofthatofA6N01S-T5basemetal,9%higherthanthatoftheMIGjoints.Fatiguepropertieswastestedindividuallywithpulsedtensilefatiguemethodintheconditionof1×107lifetime.Thetestresultsdemonstratedthatthefatiguestrengthofthejointswasalittlelowerthanthatofbasematerial,whichcouldbeupto115MPa.Butthefatiguestrengthofhybridweldingjointswas107.5MPa,whichwas23%higherthan87MPaofMIGweldingjoints.

简介：FlameheatingcombinedwithwatercoolingwasusedtostraightenA6N01aluminumalloyweldedjointandeffectofflameheatingpassonitsmicrostructureandmechanicalpropertieswasstudied.ResultsshowedthattheflameinducedtheprecipitationandgrowthoftheMg2SiphaseontheAlsubstrateforthethermalagingA6N01aluminumalloyweldedjoints,thusitledthedecreaseofmicro-hardnessandtensilestrengthoftheA6N01aluminumalloyweldedjointwiththeincreaseoftheheatingpass.However,thefatiguepropertyoftheflameheatedjointwasimprovedbecausetheMg2Siprecipitationhinderedtheinitiationandpropagationofthefatiguecrack.

简介：Inthispaper,Ni-basedalloycompositecoatingreinforcedbyTi(C,N)particleswasfabricatedonthemildsteelthroughlasercladdingtechnology.Themicrostructureoflasercladdinglayerwasanalyzedbymeansofopticalmicroscopy(OM),X-raydiffraction(XRD)andscanningelectronmicroscopy(SEM).ThewearresistancetestofthecoatingwasevaluatedusinganM-2000tester.TheresultsshowedthattheNi-basedcompositecoatinghadanabilityofrapidsolidificationtoformdendriticcrystalsmicrostructureconsistingofTi(C,N)particulatesuniformlydistributedinthematrix.ItwasfoundthatsomeTi(C,N)particlesaresimilartoberoundinshape,andtheothersareirregular.LasercladdinglayerreinforcedbyTi(C,N)particulateswasfoundtopossessgoodwearresistanceproperty.

简介：