简介：YbAl3(BO3)4crystalofgoodopticalqualitywasgrownbythefluxmethod.ThestructureofYbAl3(BO3)4crystalwasdeterminedbysingle-crystalX-raydiffraction.TheexperimentshowsthatYbAl3(BO3)4belongstothedoubleborateswithatrigonalstructure.ThespacegroupisR32anditsunitcellconstantsweremeasuredtobea=0.92965nm,c=0.72129nm,V=0.53673nm3,Z=3.Thetransmittancespectraweremeasured.Thecut-offofYbAl3(BO3)4crystalis216nm,andtherearetwoabsorptionpeakslocatedat940and975nmfrom190nmto2600nm.ThethermalpropertiesofYbAl3(BO3)4crystalwerestudiedforthefirsttime.Theaveragethermalexpansioncoefficientsweredeterminedtobe2×10-6/℃,9.5×10-6/℃alonga-andc-direction.ThespecificheatofYbAl3(BO3)4crystalwasmeasuredtobe0.6695J·(g·℃)-1atroomtemperature.AllresultsindicatethattheYbAl3(BO3)4crystalisanexcellentstoichioimetriclasermaterial.

简介：TheNd3+3.2%(atomfraction):KGd(WO4)2crystalwasgrownbyKyropoulosmethod.TheabsorptionspectrumandfluorescencespectrumofNd3+:KGWcrystalweremeasured.Theabsorptioncrosssectionsat808nm(0.6799×10-20cm2)werecalculated,andtheoutputwavelengthoffluorescenceis1064and1351nm.Thediode-pumpedlaserwasoperatedbothinthefree-runningandpassivelyQ-switchedoperatingmodes.Themaximumlaseroutput(1064nm)is326mWwith62.7%slopeefficiencywheninputenergyis900mW.ThebeamqualityfactorM2≈1.1.Thegreenlightof532nmisobtainedinfrequencydoublingoperation.ThelaserispassivelyQ-switchedbyusingCr4+:LuAGassaturableabsorber.Thepulsewidthis170nsatrepetitivefrequencyof15kHZ.

简介：LiNbO3单个水晶与的生长嗯(3+)并且Zn(2+)共同做使用布里奇曼方法和它的典型吸收系列和荧光系列被报导。开始包含Zn(2+)(3%)的大尺寸的晶体并且嗯(3+)(0.6%)用象0.81.5公里·h的生长率那样的优化条件与好光质量被获得(?1)并且大约3035°C·厘米的一个温度坡度(?1)越过稳固液体的接口和封上的铂坩锅。X光检查衍射和微分热分析(DTA)被用来描绘晶体。结果显示集中嗯(3+)在晶体，他们的吸收紧张，和他们的荧光紧张的离子在晶体从底部减少到顶。为水晶的上面的部分，然而，起来变换荧光紧张比800或970nm泵激动的更低的部分的高。水晶格子，他们的结构的缺点和他们的有效分离的效果嗯(3+)离子关于起来变换荧光紧张的变化被讨论。

简介：ThesinglecrystalgrowthofstoichiometrichostluminescentcrystalNa5Eu（WO4）4hasbeeninvestigated.UsingNa2WO4asaflux,theoptimumconditionstogrowapuresinglecrystalbyflux-slow-coolingmethodhavebeendetermined.Ahighopticalqualitysinglecrystalofdimention4.5mmhasbeengrown,whichisthelargestoneasweknowsofar.Themicro-hardnessofNa5Eu（WO4）4singlecrystalis3.46×103MPa.Itsrefractiveindexis1.81inwhitelightwavelengthregionandthespecificgravityis5.65g/cm3.Thefluorescentandexcitationspectrahavebeendeterminedandthereasonofthefluorescentquenchof5D2and5D1to7FjofEu3+canbeexplainedasmulti-phononnon-radiationtransition.

简介：空CuO-CeO2-ZrO2nano粒子被作为反溶剂把甲醇用作溶剂和supercritical二氧化碳与supercritical反溶剂仪器准备。二个关键因素(即，压力和温度)被调查探索催化剂结构和药品化学药品性质的效果(即，形态学，减少的性质，氧存储能力和特定的表面区域)。产生材料与X光检查衍射(XRD)被描绘，高决定传播电子显微镜学(HRTEM)，Brunauer-Emmett-Teller(赌注)，氢温度规划了减小(H2-TPR)和氧存储能力(振荡)测量分别地。试验性的结果证明更低的温度支持了空结构nano微粒的生产。粒子形态学也显著地变化了，即稳固的构造然后首先被转移到空结构回到稳固的建设。为获得空nano粒子的最佳的条件在45点被决定