53 个结果
  • 简介:SiliconoxynitridewasaddedinshapedAl2O3-SiC-Crefractorymaterialtoimprovetheslagresistanceinthispaper.Optimumaddingquantityofsiliconoxynitridepowderwasalsostudied.TheresultsshowthattheslagresistanceofAl2O3-SiC-Cshapedrefractoryisimprovedwhen2%or3%Si2N2Oisadded.AreasonableamountofSi2N2OaddedintoAl2O3-SiC-Cshapedrefractorycanproducesiliconoxideintotheslag,whichcanimprovetheviscosityofslagandpreventtheslagerosionandpenetration.

  • 标签: SLAG resistance SILICON OXYNITRIDE alumina-silicon carbide-carbon
  • 简介:Thecorrosionofrefractoriesresultsfromreactivetransport,namely,transportofagentsandchemicalreactionsoftheseagentswithimpregnatedmedium.Ononehand,thetransportinvolveseitherdiffusionorimpregnationdependingonthestateofthecorrosiveagentsandthemicrostructureofthehostmedia.Ontheotherhand,chemicalreactionsmaybeverynumerousandcomplex.ThisstudyfocusedonthereactiveimpregnationofAl2O3-CaOslagintoporoushighaluminarefractory.Thetransportpropertiesoftherefractorymaterialwereidentifiedbymeansofadedicatedcapillaryrisingtest.ChemicalreactionsbetweenthesolidhighaluminaskeletonandAl2O3-CaOslaginvolvesuccessivedissolution/precipitationmechanismsformingaluminatesoflime.Contrarytothethermodynamicpropertiesofthebinarysystem,thekineticsofthesesolid/liquidreactionsisnotwellknown.Corrosiontestsassociatedwiththequenchingmethod,XRDanalyseswereperformedforabetterunderstandingofthekinetics.Theresultsofthisstudyopenupacouplingapproachforpredictingthecorrosionwearofrefractory.

  • 标签: 高铝耐火材料 反应机制 浸渍介质 氧化钙 腐蚀剂 氧化铝
  • 简介:β-sialon/alumina/silicamixturesweresinteredinflowingnitrogenat1500℃and1600℃respectively.ThesinteringpropertiesandmorphologyofsampleswereinvestigatedbySEM,EDSandXRD.Resultsshowthatsinteredpropertiesofthesamplesareinfluencedbysoakingtemperaturesandcompositions.Bulkdensitiesofsamplesareincreasedwiththeincreaseofthesoakingtemperature,whereastheapparentporositiesaredecreased.Masslossofthesinteredsamplesat1500℃islowerthanthatat1600℃,butallthemasslossremainsapproximatelyconstantwiththeincreaseofsialoncontent.Fromthepointofthermodynamicanalysis,ComplexchemicalreactionstakeplaceinsamplesduringsinteringprocessandthevolatileofSiO(g)isresponsibleforthemasslossofsamples.Comparedtocrosssectionmicrostructureofβ-sialon/Al2O3/SiO2mixturessinteredincokepowderbedconsistingofthedensecenterwithwell-developedcolumnofsialonphase,thetransitionalpartwithneedlelikegrainnitrogen-containingphaseandtheloosepartwithshortgranularAl2O3phase,thoseofmixturessinteredinflowingnitrogenisofwell-developedsialonindensecenterandslightlyloosepartwithsialondebris.

  • 标签: 硅铝氧氮聚合材料 氧化铝 硅石 高温条件 耐火材料
  • 简介:MicrostructureandgrainboundarycharacterofhotpressedbinaryAl2O3(mullite,ZrO2)-SiCompositesandquaternaryAl2O3-mullite-ZrO2-SiCcompositewerestudiedbyelectronmicroscopyandmicroanalysis,ResultssuggestthatthereexistgrainboundarysolidsolutionsduetoelementaldiffusionnearSiCandmatrixoxidesgrainboundaries.

  • 标签: 微观结构 氧化铝 AL2O3 ZRO2 碳化硅 氧化锆
  • 简介:LowcementAl2O3-SiO2castableswaspreparedusingsupergradebauxite(w(Al2O3)>85%)asaggregate,brownfusedcorundum,siliconcarbide,Secar71CAcement,α-Al2O3micropowderandmicrosilicaasfinepowders.TheinfluenceofSiC(0,5wt%,10wt%,and15wt%)onresistancetoPbO-richslagwasinvestigatedbystaticcrucibleslagtest(1300℃for5h,inair).TheslagcorrosionmechanismofthecastableswasanalyzedbymeansofSEM,EDSandXRD.TheresultsshowthattheresistanceofAl2O3-SiO2castablestoPbO-richslagisimprovedobviouslybytheadditionofSiC.ThecorrosionmechanismofthePbO-richslagcanbediscribedasthatPbOintheslagreactswithSiO2andCaOinAl2O3-SiO2castables,forminglow-meltingcompounds(suchasPbO·SiO2and2PbO·SiO2).

  • 标签: 二氧化硅 氧化铝 硅含量 氧化铅 碳化 料渣
  • 简介:Thisworkinvestigatedthethermo-gravimetric(TG)changeandexplosionresistanceofultra-lowcementAl2O3-SiO2castablesaddedwith0,5%,10%,15%and20%of≤74μmrawbauxitepowderscontaining72.8%Al2O3,respectively.Thecastableswerepreparedusingwhitefusedaluminaasaggregate,powdersofwhitefusedalumina,fusedmullite,α-Al2O3ultrafines,3%CAcementand5%microsilicaasthematrixportion.TGchangeofthecastableswasinvestigatedbyathermo-gravimetricanalyzerforlargesizespecimen.Whentherawbauxiteadditionislessthan10%,themass-losingbehaviorofthecastablesissimilartothatwithoutrawbauxite,tendingtoreachaconstantmassaround400℃,beforewhichthemass-lossismildandproducinglittledestructiveinfluence.Withmorethan10%rawbauxiteaddition,however,themass-lossincreasessignificantly,andthetemperaturetoreachaconstantmassincreasesto600℃orhigher,unfavorabletostructuralstabilization.Withtherawbauxiteadditionupto20%,nonegativeinfluenceonexplosionresistanceisfound.

  • 标签: 氧化铝微粉 铝土矿石 超低水泥 二氧化硅 浇注料 热行为
  • 简介:Reactionsintereddensezirconia-mullitecompositeswerepreparedbyisostaticallypressingfromzirconflourandreactivealuminawithdifferentproportionsofTiO2andCr2O3additives.Thepressedcompactsweresinteredatdifferentelevatedtemperatureswithvariablesoakingtimes.Microstructuresandphasedevelopmentinthesinteredcompactswereanalysedtoassesstheinfluenceoftheadditivesonthepropertiesofthezirconiamullitecomposite.

  • 标签: REACTION SINTERING ZIRCONIA-MULLITE ADDITIVES microstructure isostatic
  • 简介:Siliconcarbide(SiC)-alumina(Al_2O_3)-mullite(Al_6Si_2O_(13))compositepowderwassuccessfullysynthesizedat1550℃for5hviacarbothermalreductionreaction,andtheeffectsofvariousmassratiosofactivecarbontoflyash(0.38,0.44and0.58)onthephasecompositionandmicrostructureofproductswereinvestigated,andtheformationprocessofthepowderwasalsoanalyzedindetail.Theproductsmainlyconsistofβ-SiC,α-Al_2O_3,Al_6Si_2O_(13)andFeSi.IncreasingcarboncontentfavorsthedecompositionofAl_6Si_2O_(13)andformationofSiC.Theaverageparticlesizeofβ-SiCandα-Al_2O_3isabout1μmandthatofAl_6Si_2O_(13)is5-10μm.TheformationprocessofSiC-Al_2O_3-Al_6Si_2O_(13)powderincludesthedecompositionofmulliteinflyashandformationofSiC.

  • 标签: 碳热还原反应 复合粉体 粉煤灰 相形成 显微结构 物相组成