简介:SomenewNi-saving25Crduplexstainlesssteels(DSS)havebeendeveloped.Theresultsindicatethatthealloyhasabalancedferrite-austeniterelationafterhotforgeandsolidsolutiontreatmentat1000℃.TheelementsWandCuhaveamarkedeffectonthemicrostructureofthealloy.ThepittingpotentialofthesteeladdingWandCuelementsreachesthemaximumvalueof435mV.Thetensilestrengthandpercentageofareareductionofallsteelsinthispaperare800-900MPaand60%-70%,respectively.Thetensileelongationsofthealloysareallabove30%.Theexperimentalsteelshavegoodcorrosionandmechanicalproperty.
简介:Usingmetallographicobservationandmechanicalmeasurement,themicrostructureandmechanicalpropertiesofGH4169Galloyhasbeeninvestigated.Theeffectofthephosphorus,borontraceelementsonmechanicalpropertiesoftheGH4169Galloyarecomparedandanalyzed.Theresultsshowedthatthehot-workabilityoftheGH4169Galloyisverygood.ThestressrupturespropertiesofGH4169Galloyisover3timesthanthetraditionalGH4169alloy.
简介:介绍了厚规格Q390GJC-Z25高强度钢板的研发工艺及试制过程。试制结果表明:采用Nb、V、Ti复合微合金化、控轧控冷、正火热处理工艺生产的厚规格Q390GJC-Z25钢板组织均匀、晶粒细小,各项力学指标均符合国标要求,探伤达到Ⅰ级。
简介:Improvingtheunitheatefficiency,reducingcoalconsumptionandtheemissionofCO2andmeetingtherequirementsofenvironmentalprotectionandenergyconservationisthegoaloftheboilerandthepowerindustry.Developmentsoflargecapacityandhighparameterultra-supercritical(USC)unitsarethetendencyofthepowerindustry.ThereisnodoubtthatthedevelopmentofUSCunitsisbasedonthedevelopmentofmaterials,especiallythematerialsusedforsuper-heaterandreheaterinhigh-temperatureUSCboiler.Duetothelongtimeexposuretotheharshenvironment,suchasbearingthe600℃steamoxidation,andwithstandingthecorrosivefluegasandflyasherosion,thematerialsrequirenotonlygoodhigh-temperaturestrength,butalsoagoodcorrosionresistance.Inconsiderationoftherequirementscitedabove,foreigncountrieshaddevelopedTP310HCbN(07Cr25Ni21CbN)austeniticheat-resistantsteel.However,thedomesticdemandsforthismaterialstilldependonimportandthecostishigh,sotheboilerandthepowerindustryexpectseagerlythatthesesteelscanbeproducedbydomesticmetallurgicalindustry,especiallyBaosteel,toreplacetheimportedproducts.Inordertosatisfytherequirementsofdomesticmanufacturingsuper-heaterandreheaterusedinultra-supercriticalpowerboiler,afterdevelopedT23、T91、T92、S30432highpressureboilertube,BaosteelbegantodevelopTP310HCbN(07Cr25Ni21CbN)austeniticstainlesssteeltubeinJanuaryof2007.Thisstudydescribesthecompositiondesign,themanufacturingprocessofproduct,andtheassessmentofperformanceofBaosteel’sTP310HCbN(07Cr25Ni21CbN).ThedataindicatesthatpropertiesofBaosteel’sTP310HCbN(07Cr25Ni21CbN)conformtotheASMESA-213standardandGB5310standard,soitcansubstitutetheimportedproductsandissuitableformanufacturingpowerstationboilerofgreatcapacityandhighsteamparameters.
简介:通过实验解读微淬火(超临界淬火)的本质:α→γ相变与磁畴瓦解同步;(高温型)板条马氏体相变与"司南鱼"超磁化共生;微淬火(微观层面)囊括了所有已知超塑形变类型,是获取(宏观层面)高频热轧超塑性的最佳工艺;微淬火高频热轧超塑性无须具备诸多苛刻条件,是一种独特的理想的超塑性。