简介：EffectofCe-Mg-Si(lightRE)andY-Mg-Si(heavyRE)nodulizersonthemicrostructuresandmechanicalpropertiesofheavysectionductileironwasinvestigatedtodevelopthematerialofspent-nuclear-fuelcontainers.Twoas-castsweretreatedbythesamequalitypercentageoflightREandheavyRE,respectively.Fourpositionswerechosentostandfordifferentsolidificationcoolingratesofspecimens.Thetensilestrength,elongationandimpacttoughnessofspecimenstreatedbyheavyREwereallhigherthanthoseofthespecimenstreatedbylightRE.Withthedecreaseofcoolingrate,themechanicalpropertiesoftwospecimensdecreased,andthefracturemorphologychangedfromductilefracturetobrittlefracture.TheimprovingeffectofmechanicalpropertiesbetweenheavyREandlightREwasobviousduetothebetteranti-degradationpropertyofheavyRE.Whilethesolidificationprocesslastedformorethan250min,theimprovingeffectwasnotobviousduetoseriousspheroidalizationdecaying.

简介：

简介：

简介：ToevaluatethepossibilityofusingGd-Si-Gealloysinmagneticrefrigerators,samplesofGd-Si-GealloysweremadeofdomesticGd.Themagnetocaloriceffectofsampleswasestimatedbymagneticentropychange(-ΔSm)calculatedfromM-HcurvesaccordingtoMaxwellrelation.ThefirstorderphasetransformationwasdestroyedduetotheimpuritiesinthecommercialGd,sothatnogiantmagnetocaloriceffectwasfound.ThesamplesmadeofpurifiedGdexhibitfirstorderphasetransformation,andthe-ΔSmisbasicallyconsistentwiththepublisheddataofAmeslaboratory,USA.ThisworkprovesthatGd-Si-GealloysmadeofdomesticGdcanbeutilizedinmagneticrefrigerators.

简介：介绍了热轧带钢(卷)表面氧化皮在轧制过程中的控制技术理念、热轧带钢加工前表面预处理的方法及各自优缺点,为下游制造企业在选择钢板表面预处理时提供了参考依据,或钢厂直接提供清洁绿色、无污染的优质热轧产品。

简介：ＭｏｓｓｂａｕｅｒＥｆｆｅｃｔｏｆＲａｐｉｄｌｙＱｕｅｎｃｈｅｄＡｌ－Ｆｅ－Ｖ－Ｓｉ－ＭｍＡｌｌｏｙｓＷａｎｇＪｉａｎｑｉａｎｇ（王建强），ＣｈａｏＹｕｅｓｈｅｎｇ（晁月盛），ＺｅｎｇＭｅｉｇｕａｎｇ（曾梅光），ＺｈａｎｇＢａｏｊｉｎ（张宝金），Ｃｈ...

简介：

简介：针对方大特钢公司60Si2Mn弹簧扁钢产品出现剪切端面裂纹问题,进行裂纹检测、剪切温度试验和不同温度下力学性能检测;分析发现剪切时的温度对裂纹产生的影响,发现剪切裂纹是剪切应力作用于偏析较严重部位形成的裂纹源在残余应力释放过程中扩展形成的横向裂纹.根据分析结果,在生产实践中分别对炼钢、轧制工序采取相应措施,有效控制了弹簧扁钢的剪切端面裂纹.

简介：

简介：Differentrareearth(RE=La,Ce,Pr,Nd,Sm,Y)andCumodifiednickelcatalystsforhydrogenproductionfrommethanedecompositionweresynthesizedbyasol-gelprocessandmethod.ThecatalystswerecharacterizedoranalyzedthroughBrumauer-Emmett-Teller(BET),X-raydiffraction(XRD),scanningelectronmicroscopy(SEM),transmissionelectronmicroscopy(TEM)techniques.Andthehydrogenproductionperformancewasalsoevaluatedbyafixed-bedandmicro-reactiontechniquewithCH4→C+H2asaprobereaction.Theresultsshowedthatrareearthmodificationhadplayedagreatrolefornickelcatalysts,forexample,smallernickelparticles,goodthermalstability,highactivity,etc.Lawasthebestadditiveamongrareearthmodification.TheSEMofrareearthmodifiedcatalystsshowedorderedflower-likestructureandrareearthmodificationmadethenickelparticlesmovetothesurfaceofcatalysts.Inaddition,theSEMofnano-carbonswasalsochangedbyrareearthmodificationwithlong,narrownano-carbonfibersortubesobtained.Solidcarbonformationwaspreventedbyrareearthmodification.

简介：

简介：

简介：针对合金篦条材料表面进行等离子渗碳技术的试验研究和渗层的耐磨性能实验分析。利用等离子技术成功地在舍金篦条试样表面渗碳，使表面w（C）达到1．5％以上，渗碳层深1mm左右，表面硬度大大提高。合金篦条试样经渗碳后，在合金表面形成了碳化铬化合物，表面耐磨性能发生了质的变化。经磨损试验。耐磨性能较未经表面处理试样有较大的提高。

简介：采用LeicaDMR光学显微镜观察718中厚板表面裂纹的形貌、非金属夹杂物,采用扫描电镜/能谱仪（438VP/KEVEX）对裂纹和基体化学成分进行分析,并结合现场生产工艺参数,从非金属夹杂、裂纹形貌、连铸生产参数等方面对718中厚板表面裂纹产生原因进行了分析研究。结果表明：连铸机冷却系统存在问题,致使连铸坯局部过冷,产生热应力集中现象,导致坯料产生裂纹并且在轧制过程中进一步延伸。

简介：Thephasesandmagnetocaloriceffectinthealloys(Gd1-xErx)5Si1.8Ge2.2withx=0,0.1,0.2and0.3wereinvestigatedbyX-raydiffractionanalysisandmagnetizationmeasurement.ThesamplesweresinglephasewiththemonoclinicGd5Si2Ge2-typestructure.WiththeincreaseofErcontent,theCurietemperature(Tc)decreasedobviouslyfrom253Kofthealloywithx=0to114Kwithx=0.3.Themaximummagneticentropychangedinthesamplesof(Gd1-xErx)5Si1.8Ge2.2withx=0.0,0.1,0.2and0.3were6.88,8.32,9.59and10.24J·kg-1·K-1respectivelyintheappliedfieldchangeof0～2.0T.

简介：

简介：对304不锈钢连铸坯进行了解剖分析。分析结果表明：在25%的铸坯深振痕或渣坑缺陷试样中观察到了微裂纹或气孔。

简介：就304不锈热轧带钢表面"侧翻"和划伤缺陷产生的原因进行了分析,并提出了相应的控制措施.

简介：在实验室完成不锈钢表面机械抛光实验,通过扫描电镜观察分析表明,影响抛光缺陷的主要因素分三大类：基体硬质夹杂物、原始表面质量以及抛光工艺中的机械划伤。针对各种缺陷的产生原因,提出了相应的改进措施：通过对炼钢工艺进行夹杂物塑性化控制,减少硬质夹杂物的数量,以及通过调整后续轧制工艺,可避免表面凹坑,提高表面质量,从而较少表面抛光缺陷的产生。

简介：通过实验使用表面粗糙度测试仪测定了无氟连铸结晶器保护渣的表面粗糙度,研究了碱度R、Li_2O、TiO_2、Na_2O、B_2O_3、MgO对保护渣表面粗糙度的影响。实验证明：碱度大,Li_2O、TiO_2、Na_2O、MgO含量高的保护渣,其冷态下的表面粗糙度相对较高;保护渣的玻璃化性能随着B_2O_3含量的提高而变好,表面更加光滑;MnO含量在2%~4%时,随着的MnO含量的增加,表面粗糙度变大;MnO含量在4%~6%时,随着的MnO含量的增加,表面粗糙度变小。