Al4C3 Hydration Thermochemical Analysis for Burned Carbon-Containing Refractories with Al

(整期优先)网络出版时间:2003-01-11
/ 1
Inthispaper,X-raydiffractogramanalysisandSEMobservationofAl4C3formedathightemperaturefromcarbon-containingrefractorieswithAlhavebeencarriedout.Aluminumaddedtocarbon-containingrefractoriesreactswithC(s)toformAl4C3(s)graduallyduringheatingfrom600℃to1200℃.ItisconsideredthattheinterlockedstructureofAl4C3platecrystalspromotestheoutstandingincreaseofhotmodulusofruptureofcarbon-containingrefractorieswithAl.TheHMORofcarbon-containingrefractoriesaddedwithAladditivefrom0to5wt%increasesby2.8timesbeingfrom6.5MPato18.2MPa.AfterathermochemicalcalculationforhydrationreactionprocessesofAl4C3andH2O(g),theequilibriumpartialpressurechartofH2O(g)inH2O-Al4C3-Al(OH)3systemvsvarioustemperatureshasbeenattained.TheH2O(g)partialpressureintheairneededfortheAl4C3hydrationreactionisnomorethan10~18atmatthetemperaturebelow120℃.Itisconsideredthattheburnedcarbon-containingrefractorieswithAlisextremelyeasytohydrateandthecrackingofburnedcarbon-containingrefractoriesisgeneratedbecausethatthehydrationexpansionis2.11timesduringtransformingfromAl4C3toAl(OH)3.ThefundamentalmeasureagainsthydrationoftherefractoriesistoinsulatetherefractoriesfromH2O(g)byvariousmeanssuchaspitchimpregnationorothersealingmaterials.