Microstructure Characteristics of Interaction Layer of Zn-Al Eutectic Alloy with Al2O3p/6061Al Composites

(整期优先)网络出版时间:2004-04-14
/ 1
TheinteractionbetweenZn-AleutecticalloyandAl2O3p/6061Alcompositesinthevacuumfurnacewasinvestigated.Greatattentionhasbeenpaidtotheelementsdiffusion,themicrostructureandformationoftheinterfacebetweenZn-AIeutecticalloyandAl2O3p/6061Alcomposites.ExperimentalresultsshowthatZn-AleutecticalloyhasagoodwettingabilitytoAl2O3p/6061Alcompositesandthewettingangledecreaseswithincreasingthetemperatureinvacuum.Aftertheinteraction,aninteractionlayerformsbetweenZn-AIalloyandAl2O3p/6061Alcomposites.Thephasesintheinteractionlayermainlyconsistofα-Al(Zn),Al2O3andCuZn5resultedfromthediffusionofelementsfromtheZn-Alalloy.SeveralporositiesdistributeintheregionneartheinterfaceoftheZn-Alalloy/interactionlayer.TheamountofshrinkagevoidsintheinteractinglayerisrelevanttothepenetrationofZnelementintoAl2O3p/6061Alcompositeswhichisafunctionoftemperature.SoitisnecessarytolowerheatingtemperatureinordertolimittheZnpenetration.