简介:Sr1.995–1.5xGdxSiO4:0.005Eu2+phosphorserieswithx=0–0.08molfornear-ultravioletwhitelight-emittingdiodes(NUVw-LEDs)weresynthesizedviasolid-statereactionmethod.XRDprofilepatternandrefinementresultsdemonstratedthatdopingGd3+ionsresultedinthephasetransformation(β-Sr2SiO4→α’-Sr2SiO4).Thephotoluminescencespectrumofthesamplewithx=0moldisplayedtwoemissionpeakscenteredat470and525nm.Thetwo-peakspectrabecameone-peakspectrawiththeGd3+concentrationincreasing.Actually,thefittingresultsdemonstratedthattheone-peakspectrawerestillcomposedoftwosingleemissionspectra.ThephotoluminescenceintensitywasimprovedandtheCIEchromaticitycoordinateswereadjustedviadopingGd3+.
简介:Organicsubstancesuchassolventandresin'seffectonluminescentcapabilityofSrAl2O4:Eu2+,Dy3+phosphorwasstudied.Someorganicsolventsandresinswereselectedforexperimentation.TheresultsindicatethatthoseorganicsolventswillnothavenegativeeffectontheappliedcapabilityofSrAl2O4:Eu2+,Dy3+phosphor.Adoptingtheorganicresinsandcoveringmethod,theafterglowluminanceofSrAl2O4:Eu2+,Dy3+phosphorwasincreasedby85.01%and82.51%.
简介:通过金相显微镜(OM)、扫描电镜(SEM)和动态热机械分析仪(DMAQ800)等分析手段研究粉末冶金法制备的Ti-47Al-2Cr-2Nb-0.2W(原子分数,%)合金微观组织对其阻尼性能的影响。研究结果表明:Ti-47Al-2Cr-2Nb-0.2W合金初始组织为近γ组织,其阻尼性能最差,在振幅为100μm时,损耗因子仅为0.007;在1330℃下保温15min空冷可获得细小全层片组织,层片晶团的平均尺寸约为200μm,其损耗因子在振幅为100μm时达到0.012。随温度升高或保温时间延长,层片尺寸和晶团尺寸明显增大,合金阻尼性能下降,保温120min时层片晶团的平均尺寸约为510μm,其损耗因子在振幅为100μm时为0.009。细小全层片的阻尼性能最好,而双态组织的阻尼性能介于近γ组织和细小全层片组织之间。
简介:ThemeasurementsoftemperaturedependenceofthemagneticsusceptibilityofLa1-xSrxCoO3perovskiteoxidesatdifferentSrdoping(0≤x≤0.5)andannealingtemperaturewerepresented.Forthesamplewithx=0.1,ashoulderwasobservedaround150K,andapeakwhichisonefeatureofspinglassappearedaround50Kinthecurveofsusceptibilityversustemperature.Thehigh-temperature(250~420K)susceptibilityfitswellwithCurie-Weisslawforallsamples.WeissconstantandeffectivemagneticmomentweredeterminedandtheirvariationswithSrdopingandoxygenannealingconditionwereobtained.TheWeissconstantincreasesmonotonouslywithSrcontentforx>0.2.Thevaluesofeffectivemomentswereinterpretedwiththespinstateofcobaltions.Studiesonthesusceptibilitiesofthesampleswithx=0.2underdifferentpreparationtemperaturesandannealingtemperaturesshowthattherisingofsinteringtemperatureandannealingtemperaturewillincreasethepara-ferromagnetictransitiontemperature,andreducetheeffectivemomenttonormalvalue.OurresultshowsthatbothCo3+andCo4+ionsshouldbeinISstateafterannealingandtheoxygenannealingcausesthetransitionofCo3+spinstatefromHStoIS.
简介:探讨了在大生产条件下4Cr5MoSiV1钢的脱碳层测定原则。结果表明,金相法测定结果较准确且操作简便