简介:Bead-on-plateCO2laserweldingof1000MPagradetransformationinducedplasticity(TRIP)steelwasconductedunderdifferentweldingpowers,weldingspeedsandshieldgases.Themacrostructuralandmicrostructuralfeaturesoftheweldedjointwereinvestigated.Theincreaseofweldingspeedreducedthewidthoftheweldbeadandtheporositiesintheweldbeadresultingfromthedifferentflowmodeofmeltedmetalinweldpool.ThedecreaseofweldingpoweroruseofshieldgasofheliumalsocontributedtothereductionofporosityinBead-on-plateCO2laserweldingof1000MPagradetransformationinducedplasticity(TRIP)steelwasconductedunderdifferentweldingpowers,weldingspeedsandshieldgases.Themacrostructuralandmicrostructuralfeaturesoftheweldedjointwereinvestigated.Theincreaseofweldingspeedreducedthewidthoftheweldbeadandtheporositiesintheweldbeadresultingfromthedifferentflowmodeofmeltedmetalinweldpool.Thedecreaseofweldingpoweroruseofshieldgasofheliumalsocontributedtothereductionofporosityintheweldbeadduetothealleviationofinducedplasmaformation,thusstabilizingthekeyhole.TheporosityformationintimatelycorrelatedwiththeevaporationofalloyelementMninthebasemetal.Thelaserweldedmetalhadsamemartensitemicrostructureasthatofwater-quenchedbasemetal.Theweldingparameterswhichincreasedcoolingrateallledtofinemicrostructuresoftheweldbead.