简介：

简介：Layeredcathodematerialsofhigh-temperaturelithiumbatteries,LiNi1/3Mn1/3Co1/3O2aresynthesizedbyasol-gelmethodwithvariationinfinalsinteringtemperatureforboreholeapplications.Thestructure,morphologyandhigh-temperaturedischargeperformanceoftheseresultingproductsareinvestigatedbyX-RayDiffraction（XRD）,scanningelectronmicroscopy（SEM）,laserparticlesizeanalysis,galvanostaticandpulsedischarge.Theresultsofstructuralanalysisindicatethatthesamplesinteredat800℃hasthecharacteristicsofgoodcrystallinity,narrowsizedistributionandlargespecificsurfaceareaatthesametime.Thedischargeexperimentsalsoindicatethatthissamplehasthebestelectrochemicalproperties,withthemaximumdischargecapacitiesof314.57and434.14mAh·g-1at200and300℃respectivelyandtheminimumcellinternalresistancesatbothtemperatures.

简介：以氧化石墨、五水硝酸铋等为原料，通过液相化学沉积法制备出Bi2O3／氧化石墨烯（Bi2O3／GO）复合催化剂，采用扫描电镜（SEM）、透射电镜（TEM）和X-射线粉末衍射（XRD）对产物的粒子形貌、粒径和物相结构进行了表征，并考察了Bi2O3／GO复合催化剂对双基推进剂燃烧性能的影响，结果表明，产物中Bi2O3以球状粒子的形式均匀地负载在氧化石墨烯表面，平均粒径约40nm。Bi2O3／GO复合催化剂能明显改善推进剂的燃烧性能，使推进剂的燃速提高了139％f4MPa），压强指数（14～20MPa）从0．650降低至0．253，降低了61．0％。

简介：具有上转换功能的纯相Yb3＋／Er3＋共掺杂β-NaYF4上转换微米管通过水热法在180％下反应24小时得到。为更好地利用太阳能并提高降解有机物的光催化效率，尝试将Ti02与NaYF4进行复合，形成Ti02／NaYF4复合材料来对Ti02纳米颗粒进行改性。我们研究了三种不同的复合方法，并对其在太阳光下进行光催化降解罗丹明水溶液的效率进行测试分析。结果表明，Ti02纳米颗粒紧密复合在NaYF微米管表面的复合材料具有相对其他两种合成方法更佳的催化活性，并且比无复合的纯Ti02纳米颗粒的催化效率提高了两倍。催化效率的提高可能是由于在两相进行复合时，在复合界面形成了异质结，该异质结有利于太阳光的吸收和催化效率的提高。

简介：用固相反应法制备了LnBaCo2O5＋δ（Ln=Gd，Nd，Sm，Pr）-Ba0．5Sr0．5Co0．8Fe0．2O3-δ（质量比为1：1）4种双相混合导体膜。通过XRD分析可知，除了PrBaCo2O5＋δ和Ba0．5Sr0．5Co0．8Fe0．2O3-δ（KSCF）复合时发生明显反应外，其它3种复合膜在复合过程中均显示了良好的化学兼容性。4种双相膜在850℃时透氧率最高的是NdBa-Co2O5＋δ-Ba0．5Sr0．5Co0．8Fe0．2O3-δ（约为0．28mL／（cm2·min））。

简介：用溶胶-凝胶法制备了系列掺杂（La0.8Ln0.2）2/3Ca1/3MnO3（Ln=La，Ce，Pr，Nd，Sm，Eu）纳米级晶体。对比在La被其它镧系元素部分替代后，引起的A位离子平均半径的改变和磁矩变化对电输运及磁阻性能的影响，实验分析表明，各个样品在同样大小磁场下的磁电阻存在较大的差别，样品的磁电阻随原子序数的增加而明显变大，由镧系收缩引起晶格畸变所产生的本征磁电阻占主导地位，随着外加磁场的增加，不同掺杂样品间的峰值电阻差异被弱化；各掺杂样品间的转变温度差与掺杂离子半径差和磁矩差密切相关，且离子半径的差异对转变温度的改变贡献更大。