简介：TheeffectofAl-3Ti-0.2C-5Sr(wt%)grainrefinerontherefiningperformanceandmodificationofA356alloywasinvestigatedusingopticalmicroscope(OM).ThemorphologyandcrystalstructureofternaryAl-Ti-SrphasesinAl-3Ti-0.2C-5Srrefinerwereanalyzedbyscanningelectronmicroscopy(SEM)andtransmissionelectronmicroscopy(TEM).TheresultsshowthattheternaryAl-TiSrphasesinAl-3Ti-0.2C-5SrrefinercanpromotethegrainrefiningefficiencyofA356alloy.TheternaryAl-Ti-Srphasesco-existintwomorphologies,i.e.,blocky-likephaseandsurround-likephase,besides,whichbothhavethesamechemicalcompositionofAl_(34)Ti_3Sr.ThecrystalstructureofAl_(34)Ti_3Srisface-centeredcubic,andthelatticeparameterisdeterminedtobeabout1.52nm.

简介：研究1Cr17Ni2不锈钢中不同δ铁素体相含量变化分别在FeCl3溶液和HNO3＋HF溶液中的耐腐蚀行为。通过腐蚀失重率计算及光学金相显微镜、扫描电子显微镜的观察发现：在FeCl3溶液中,δ铁素体的存在减弱了1Cr17Ni2不锈钢的耐腐蚀性能,δ铁素体是优选腐蚀相;而在HNO3＋HF溶液中,δ铁素体的存在增强1Cr17Ni2不锈钢的耐腐蚀性能,优选腐蚀相则变成了回火索氏体。通过表面腐蚀形貌表征可以实现反推其受到腐蚀介质环境的性质,为1Cr17Ni2不锈钢腐蚀失效与预防提供可行的方法和依据。

简介：研究热挤压Al5083/B4C纳米复合材料的显微组织表征和力学行为。Al5083和Al5083/B4C粉末在氩气气氛和旋转速度400r/min条件下球磨50h。为提高伸长率，将球磨粉末与30%和50%（质量分数）平均粒径>100μm和<100μm未球磨粉末进行混合，然后进行热压和热挤压，挤压比为9:1。采用光学显微镜、扫描电子显微镜、能谱、透射电子显微镜、拉伸和硬度测试研究了热挤压合金。结果表明，机械球磨和B4C颗粒使Al5083合金的屈服强度从130MPa提高至560MPa，但伸长率急剧下降(从11.3%降至0.49%)。添加平均粒径<100μm未球磨颗粒可提高合金的塑性但降低拉伸强度和硬度，而添加平均粒径>100μm未球磨颗粒同时降低拉伸强度和塑性。随着未球磨颗粒含量的增加，断裂机理从脆性断裂转变为韧性断裂。

简介：基于刀具磨损和钻孔尺寸误差等多个性能指标，对B4C颗粒增强铝合金切削加工参数进行评估和优化。通过Taguchi的L27，3水平4因子正交阵列进行实验设计。研究结果表明：磨粒磨损和积屑瘤一般在刀具磨损时形成，同时，边角磨损也具有重大意义。影响切削刀具的侧面磨损主要决定因素是合金中的颗粒质量分数，其次分别是进给速率、钻头的硬度和主轴转速。在所有使用的刀具中，有TiAlN涂层的硬质合金钻头在刀具磨损以及孔尺寸方面具有最佳性能。灰关系分析表明：钻头材料的影响比进给速度和主轴转速的影响更大。在最佳的钻探参数下可以得到最小的刀具磨损和孔直径误差。