简介:针对无铅锡钎料润湿性的影响因素,通过对无铅锡钎料(5n99.3Cu0.7)在同一钎焊时间不同钎焊温度下以及同一温度不同钎焊时间的润湿性的研究(试验温度在推荐的最佳钎焊温度范围内),得出温度和钎焊时间对无铅锡钎料(Sn99.3Cu0.7)的润湿性的影响趋势。研究结果表明:钎焊温度升高、钎焊时间延长,可不同程度提高润湿力。
简介:Sn-dopedTiO_2nanoparticleswithhighsurfaceareaof125.7m~2·g~(-1)aresynthesizedviaasimpleone-stephydrothermaimethodandexploredasthecathodecatalystsupportforprotonexchangemembranefuelcells.ThesynthesizedsupportmaterialsarestudiedbyX-raydiffractionanalysis,energydispersiveX-rayspectroscopyandtransmissionelectronmicroscopy.Itisfoundthattheconductivityhasbeengreatlyimprovedbytheadditionof30mol%SnandPtnanoparticlesarewelldispersedonTi_(0.7)Sn_(0.3)O_2supportwithanaveragesizeof2.44run.ElectrochemicalstudiesshowthattheTi_(0.7)Sn_(0.3)O_2nanoparticleshaveexcellentelectrochemicalstabilityunderahighpotentialcomparedtoVulcanXC-72.Theas-synthesizedPt/Ti_(0.7)Sn_(0.3)O_2exhibitshighandstableelectrocatalyticactivityfortheoxygenreductionreaction.ThePt/Ti_(0.7)Sn_(0.3)O_2catalystreservesmostofitselectrochemicallyactivesurfacearea(ECA),anditshalfwavepotentialdifferenceis11mV,whichislowerthanthatofPt/XC-72(36mV)under10hpotentialholdat1.4Vvs.NHE.Inaddition,theECAdegradationofPt/Ti_(0.7)Sn_(0.3)O_2is1.9timeslowerthancommercialPt/XC-72under500potentialcyclesbetween0.6Vand1.2Vvs.NHE.Therefore,theassynthesizedPt/Ti_(0.7)Sn_(0.3)O_2canbeconsideredasapromisingalternativecathode,catalystforprotonexchangemembranefuelcells.