简介：本文在0.0016％亚硝基R盐-0.75摩尔/升氯化铵,pH=9条件下,镍于-0.42伏(VS.S.C.E.)产生吸附催化波,波形好,镍浓度在0.01～0.6微克/毫升范围内有线性关系。常见的共存离子有一定的允许量,对一些镍矿石样品的分析结果与标准值无明显偏差。

简介：Traditionally,austeniticstainlesssteels304and316havebeenemployedincoastalregionsasroofingmaterialsunfortunately,theyareexpensiveandnotfullyresistanttopittingcorrosionunderseverecoastalcorrosiveenvironment.AferriticstainlesssteelB445Rwasdeveloped.Comparedwithaustenitic316L,B445Ris①lesscostly;②uperiorcorrosionresistantwithminormaintenanceforlong-termservice;③insusceptibletothermaldistortionintheweldingseam.B445Rsheetshowsahigheryieldstrengthandlowertensilestrength,lowerelongationandlowerwork-hardeningthanaustenitic316L.Itcanbeeasilyfabricatedanddeformedjustlikeplaincarbonsteel.Afterbending180o,thereisnooccurrenceof'cracking'ornoticeable'orangepeel'.Theformabilityoftheweldingseamisalsosatisfactory.ThepittingpotentialofB445Ris650mV,largerthanthatof304and316L,asshowninFig.1.ThecorrosionrateofB445Rsubmergedin6%FeCl,solutionis0.3-0.56g/(m2?h-1),muchlowerthanthatof316L,asshowninFig.2.ThesuperiorpittingcorrosionresistanceofB445RcanbeascribedtosynergeticeffectofhigherCrandMo.Dull-finishedB445RsheetshavebeenemployedastheroofingmaterialsforGuangzhouAsianGamesArena,asshowninFig.3.About380tof1.0mmB445Rwithdullfinishwasusedforroofingpanels.About100tof0.8mmB445Rwithhairlineorfluororesinpaintfinishwasusedforsidewallpanels.Thecompositeroofbuild-up（fromuptobottom）includes:①shinglesofferriticstainlesssteelB445R;②Kalzip-typestandingseamofaustenitic304;③water-proofDFM;④structuralsteel;⑤75mmthickinsulation;⑥secondarypurlinof150mm×100mm×4.5mmofgalvaniziedQ235;⑦0.8mmthickprofiledeckofgalvaniziedQ235;⑧acousticinsulation.Theroofingshinglesorpanelswiththesamewidthbutdifferentlengthwereformedbybendingfoursidesandfixedtoa'L'shapereinforcingframesofstainlesssteelbyfasteners.The'L'frameswasconnectedtoribsofthestandingseambyacl

简介：Thedull-finishferriticstainlesssteel(FSS)sheetB445RforarchitecturalroofinghasbeendevelopedbyBaosteel.ThissteelproductexhibitsexcellentcorrosionresistancesuperiortothatofSUS316Lwithalowercost.Itcanbeeasilyformedintoroofingpanelsbyordinaryprocesses.Moreover,thethermalstrainofitislessthanSUS316Lbecauseofitslowerthermalexpansioncoefficient,anditsreflectivityislowerduetothedull-finishtreatment.Allofthesefeaturesmakeitcapableofbeingusedasarchitecturalroofingmaterialsincoastalregions.

简介：电炉厂采用100tUHP电炉短流程生产超（超）临界高压锅炉管用钢R102。通过实施精料方针、规范脱氧工艺、优化吹氩处理工艺、选择最佳二冷区配水模型、钢水低过热度浇注、控制拉速等集成的工艺，确保开发出的产品能够满足市场需求。

简介：分析了85mm厚Q345R钢板超声波探伤不合格的原因,探讨了钢板中心裂纹的形成机理,并就冶炼和轧钢工艺提出了改进措施。

简介：在pH=4.7的六次甲基四胺缓冲介质中钒(Ⅳ)与依来铬青R、CPB形成蓝紫色的三元配合物,其组成为1:3:3,λmax=590nm,表观摩尔吸光系数为4.0×104L/mol·cm,钒在0～25μg/25mL范围内遵守比耳定律,用于钢中钒的测定,结果准确可靠.

简介：粗轧机R2主传动轴是十分重要的部件，当主传动轴较长时其自重、平衡力、扭矩及附加弯矩会显著影响使用状态及寿命。通过对传动轴静态和动态两种情况的强度校核计算，分析出了R2主传动轴断裂的原因，并确定了接轴中间部位支撑力的大小，使传动轴的工作状态达到最佳。

简介：天津钢管集团公司依托世界一流的研发中心，抽调技术骨干，充实科研力量，按系统成立工艺研究组，确定2009年90万吨高附加值产品的目标和50项重点科技创新项目，集中力量进行攻关。到目前，满足用户个性化需求的130r马氏体不锈钢油套管新品研制取得新突破，批量发往油田，解决了长期困扰油田的抗二氧化碳腐蚀问题。

简介：对中温压力容器用钢板Q370R的力学性能及焊后热模拟性能进行了试验,通过统计分析试验数据,表明该钢板具有优良的低温韧性和优良的焊接性能,能用于制造中温压力容器。

简介：阐述了120~150mm特厚压力容器用12Cr2Mo1R钢板在南阳汉冶特钢采用100t转炉—LF＋VD精炼—模铸浇注—3800mm轧机轧制—热处理的工艺研制开发过程,通过合理的化学成分设计、严格的冶炼、模铸浇铸、轧制及热处理工艺控制,最终确保了120~150mm厚12Cr2Mo1R保一级探伤、保力学性能的成功研制,并实现了批量化生产。

简介：通过溶胶-凝胶法结合光催化还原法制备掺Mo^6＋附Ag的TiO2纳米颗粒,并在可见光下对酸性大红3R进行降解实验,研究其在可见光下的催化活性,并与纯TiO2、仅掺Mo^6＋或仅附Ag的TiO2进行对比。进一步讨论在可见光照射下掺杂量、焙烧温度等因素对掺Mo^6＋附Ag纳米TiO2降解性能的影响。结果表明：可见光下Ag/Mo6＋/TiO2比纯TiO2、仅掺Mo6＋或仅附Ag的TiO2显示出更高的活性,这是因为金属Mo6＋的掺杂和贵金属银的沉积使二氧化钛的吸收带边发生红移,拓宽了可见光的响应范围;Ag/Mo^6＋/TiO2催化剂的催化活性最高时的Mo^6＋掺杂量为4.5%,银的附着量为2%。焙烧温度为500℃,这种掺Mo6＋附Ag纳米TiO2对酸性大红3R的降解率可达87.6%.

简介：