简介：承钢炼铁厂300m^2高炉液压炉顶不上钟油缸底座由于小钟与油缸活塞杆行程相差60mm，每天小钟开关频繁，各部位刚性连接，使油罐底座经常被损坏。将活塞杆与平衡臂连接销于曲φ100mm改为φ80mm；油缸底座的轴承套去掉；小钟行程调到670mm；关钟时间由原7s改为10s，但磨损仍较重。1995年9月第二座高炉小钟油缸底座改为滑块式，滑块行程65mm，小种行程调整到650mm，使用效果良好。

简介：针对烧结矿运输过程中三通分料器磨损快、寿命短的问题，研制了车式三通分料器。

简介：移动分料小车位于高架料仓,主要进行物料的分料工作,实际生产中发现移动分料小车经常出现物料堵塞现象,必须停机处理。通过对故障原因进行分析,采取了对下料斗结构进行整改、头部改向滚筒移位和安装高分子耐磨衬板等措施,取得了较好效果。

简介：对10B21冷镦钢盘条出现的冷镦开裂现象,用光学显微镜、扫描电镜、直读光谱仪对缺陷部位进行了显微组织、化学成分等分析。结果表明,冷镦开裂是由钢坯裂纹缺陷所导致,且通过Ti元素的加入,杜绝了钢坯裂纹的产生。

简介：Withpricesformetalresourcessuchasnickelandmolybdenumsoaring,thereisaheightenedsenseofcrisisconcerningresourcescarcity.WhileType304,themostcommonstainlesssteel,offersexcellentcorrosionresistance,itspriceisaffectedsignificantlybythecostofnickelbecauseofits8%nickelcontent.ThestainlesssteelthathasthesamecorrosionresistanceasthatofType304anddoesnotcontainnickelandmolybdenumhasbeenrequired.JFESteelCorporationhasdevelopedanew21%Cr-0.4%Custainlesssteel,theworld’sfirstferriticstainlesssteel,whichoffersequivalentcorrosionresistancetoType304whilecontainingabsolutelynonickelormolybdenum,tworaremetals.Thenewlydevelopedsteelcontains21%chromiumwiththeadditionof0.4%copper.Thedevelopmentofthesteelisbasedonanewdiscoverythatthepassivefilmsofstainlesssteelscouldbestrengthenedbythesynergyeffectofhighchromiumcontentandcopperaddition.Copperadditionenrichesthechromiumcontentinpassivefilmsafterfieldexposure.Newlydeveloped21%Cr-0.4%CustainlesssteelisadoptedformanyapplicationsasasubstitutionforType304,includingcommercialkitchenware,buildingmaterialsandindustrialmachinery.ThesteelisexpectedtobeanewstandardofaferriticstainlesssteelasasubstitutionforType304.

简介：

简介：本文介绍了作者在难选锦矿石浮选过程中改变过去传统的选矿流程，采取集中粗选、分选精选的选矿方法，坚持饥饿加药的原则，获得了锑精矿品位为６０．６６％、锑浮选回收率为９０．０５％的较好浮选指标。

简介：Improvingtheunitheatefficiency,reducingcoalconsumptionandtheemissionofCO2andmeetingtherequirementsofenvironmentalprotectionandenergyconservationisthegoaloftheboilerandthepowerindustry.Developmentsoflargecapacityandhighparameterultra-supercritical（USC）unitsarethetendencyofthepowerindustry.ThereisnodoubtthatthedevelopmentofUSCunitsisbasedonthedevelopmentofmaterials,especiallythematerialsusedforsuper-heaterandreheaterinhigh-temperatureUSCboiler.Duetothelongtimeexposuretotheharshenvironment,suchasbearingthe600℃steamoxidation,andwithstandingthecorrosivefluegasandflyasherosion,thematerialsrequirenotonlygoodhigh-temperaturestrength,butalsoagoodcorrosionresistance.Inconsiderationoftherequirementscitedabove,foreigncountrieshaddevelopedTP310HCbN（07Cr25Ni21CbN）austeniticheat-resistantsteel.However,thedomesticdemandsforthismaterialstilldependonimportandthecostishigh,sotheboilerandthepowerindustryexpectseagerlythatthesesteelscanbeproducedbydomesticmetallurgicalindustry,especiallyBaosteel,toreplacetheimportedproducts.Inordertosatisfytherequirementsofdomesticmanufacturingsuper-heaterandreheaterusedinultra-supercriticalpowerboiler,afterdevelopedT23、T91、T92、S30432highpressureboilertube,BaosteelbegantodevelopTP310HCbN（07Cr25Ni21CbN）austeniticstainlesssteeltubeinJanuaryof2007.Thisstudydescribesthecompositiondesign,themanufacturingprocessofproduct,andtheassessmentofperformanceofBaosteel’sTP310HCbN（07Cr25Ni21CbN）.ThedataindicatesthatpropertiesofBaosteel’sTP310HCbN（07Cr25Ni21CbN）conformtotheASMESA-213standardandGB5310standard,soitcansubstitutetheimportedproductsandissuitableformanufacturingpowerstationboilerofgreatcapacityandhighsteamparameters.

简介：上期问题答案1、C。说明：不锈钢依靠形成的氧化膜起保护作用。在某些环境中，尤其是含氯化物的环境中，这种薄膜会遭到破坏或无法形成。高合金不锈钢对于此类腐蚀性环境具有较高的耐腐蚀性。

简介：通过碳分蒸发器结垢现状调查，分析了结垢形成的原因，并针对这些因素提出了碳分蒸发器结垢预防及清除措施。

简介：目前,烧结法生产砂状氧化铝的粒度问题日益受到重视。而砂状氧化铝的粒度主要由碳分氢氧化铝粒度决定,所以研究碳分氢氧化铝粒度变化规律具有重要意义。文章运用数学方法,对碳分试验所得数据进行分析,得出氢氧化铝粒度变化诸因素的影响程度大小,确定了合理的工艺条件。

简介：据浙江省经贸委发布的信息表明，2005年浙江省组织实施节电改造项目660项，年节电21．264亿kW·h，相当于节约了杭州的主要电源之一——萧山电厂这样一个中型电厂一年多的发电量。

简介：金川公司化工厂制酸一系统实用单转吸工艺流程。在扩能技改中，针对原吸收、干燥塔分酸器存在的分酸不均、分酸器易坏的缺点，用管式分馏器替代槽式分酸器。改造投产后，经实测达到干燥、吸收工艺控制指标：用LSB2材质解决了管式分酸器的耐蚀性问题：在回酸总管上加装过滤器解决了分酸孔易堵的问题；将分酸支管深埋，加补沫丝网解决了酸沫夹带。

简介：上期问题答案1、B。说明：铁素体不锈钢高温应用受限的原因，是因为当高于450℃左右时，这些钢材的蠕变强度会急剧下降。

简介：“仅赣州地区因稀土开采而造成的区域性生态破坏面积，10年间扩大了5倍。”在环境保护部卫星环境应用中心宽敞的会商大厅，巨大的屏幕上一张张稀土开采矿区生态破坏的卫星遥感照片和航拍照片触目惊心。卫星环境应用中心万华伟博士边演示边作说明。

简介：

简介：烧结料在混合过程中需加水润湿并制粒，以改善混合料透气性，增加通过料层的风量，达到提高烧结矿产、质量的目的。混合料水分的准确检测和自动控制是烧结工艺中不可缺少的环节，烧结料水分的相对稳定对烧结过程的顺利进行以及实现烧结生产优质、低耗至关重要，烧结工作者为此做了大量的工作，其中引进北京宇宏泰测控技术公司开发研制的MM710-2lCS水分测量控制系统就是一次有益的尝试。

简介：

简介：分析黏性土边坡瑞典分条法（10分法）稳定性算法和扩大分条数目的瑞典分条法稳定系数K。分析认为：黏性土土坡的稳定性在一般工程地质评价中,理论计算方法多选用费伦纽斯和泰勒提出的瑞典分条法,分条数目多选用10分法计算;分条数目在一定程度上影响黏性土土坡的稳定性K值,在一定的区间范围内,随着分条数目的增加,黏性土坡的稳定性也在相应增加。