简介:以2,2,6,6-四甲基-4-羟基哌啶、烯丙基氯和氢氧化钠为原料催化合成4-烯丙氧基-2,2,6,6-四甲基哌啶,分别研究了反应时间、原料配比、溶剂用量和催化剂用量等条件对合成4-烯丙氧基-2,2,6,6-四甲基哌啶反应的影响,确定的最佳操作条件为:反应温度为45~54℃,反应时间5h,反应物摩尔比为:n(烯丙基氯)∶n(2,2,6,6-四甲基-4-羟基哌啶)∶n(氢氧化钠)为0.45∶0.1∶0.4,溶剂用量为10g,催化剂的用量为0.2g(2,2,6,6-四甲基-4-羟基哌啶为0.1mol),收率可达到95.43%以上,纯度为99.5%。
简介:SlagcorrosionresistanceofMgOZrO2refractorieswasinvestigatedinthiswork.Theresultsindicatethatinanon-orientedelectricsteelslagsystemwithahighratioofcalciatosilica,theslagresistanceofMgOZrO2refractoriescanbedescribedasfollows:ZrO2reactswithCaOformingcalciumzirconatecompoundwhichstrengthensthematerialandblocksthechanneloftheslaginfiltration;however,inanorientedelectricsteelslagsystemwithahighconcentrationofsilicaandthelowratioofcalciatosilica,theslagcorrosionresistanceofMgOZrO2refractoriesisdifferent;ZrO2reactswithCaOformingthecalciumzirconateandsimultaneouslyonemoreproductC2Saswell;C2Scanimprovecorrosionresistancebyblindingporeandenhancingslagviscosity;therefore,itisexpectedtobethemajorreasonfortheenhancedcorrosionresistanceobservedforMgOZrO2refractories.
简介:Al2O3-MgOcastableshavebeenwidelyusedforworkingliningsofsteelladleduetotheirsuperiorhotstrengthandcorrosionresistance.Inthiswork,effectsofmicrosilica,ultrafinealuminaandMgOfinesadditionsontherheologicalbehaviorofthecastableswereinvestigatedbymeansofIBBrheometerV1.0tomeasuretorque(shearstress)undervaryingshearrates.Theresultsshowthatrheologicalpropertiesofcastablesatvaryingshearratesaresignificantlyimprovedwithincreaseofmicrosilicaadditions(from1mass%to5mass%)andcorrespondingdecreaseinwateraddition;thereisonlylittlechangeinrheologicalbehaviorwithvariationofultrafinealuminaandMgOfinesadditions.Optimumultrafinealuminaandmicrosilicaadditionsarerecommendedforcastableswithgoodrheologicalbehavior.
简介:Cr2O3canbesinteredwellat1500℃incarbon-embeddedconditionorH2atmosphere.Butthehighchromebearingrefractoriescannotreachdensificationwhensinteredat1700℃for10hinweakreducingatmosphereformedbythecombustionoffuel,anditsapparentporosityisabout18%.Thehighchromebearingrefractoriesaremainlyusedincoalgasifiers.Thetemperatureinthefurnaceisabout1500℃andtheproductsareH2andCO,whicharejustthesinteringconditionsofthedensechromerefractorieswithapparentporositylessthan10%.Thehighchromebearingrefractoriesusedincoalgasifiersmaybesinteredagainandthenshrink,destroyingthegasifierlining.Thethermodynamiccalculationshowsthatitissafeaboutthehighchromebearingrefractoriesusedingasifiers.Itisalsoexplainedthatthehighchromebearingrefractoriescan’tbesintereddenselyinweakreducingatmosphereformedbythecombustionoffuel.Thenewsinteringtechnologiescanbeusedtoimprovethebulkdensityofthehighchromebearingrefractories.