简介:BondingofAl2O3tocuisperformeddirectlyusingTifoilattemperatureof1273K.Themicrostructureofthejointinterfaceisinuestigatedthroughscanningelectronmicroscope(SEM),electron.probemicroanalysis(EPMA)andX-raydiffraction(XRD).theeffectoftheinitialtifoilthicknessonthereactionlayerthicknessandthejointStrengthareinvestigated.
简介:本文介绍了低温(-50℃)乙烯球罐制造和焊接技术,制定了球罐制造工艺流程和球壳板成形工艺,通过试验确定了焊接预热温度、层间温度和后热温度,并正确选择了焊接材料。制定了乙烯球罐的焊接工艺规范,并成功地完成了低温(-50℃)乙烯球罐的制造和焊接。
简介:ThispaperintroducesabrazingprocessbetweenAl_2O_3ceramicandInvaralloy.Al_2O_3canbebrazedwithInvareffectively.TheinterfacialstructureofAl_2O_3/Invarjointcanbeexpressedas:Invar/Ag(s,s)+Cu(s,s)+Fe_2Ti(zoneⅠ)/Ag(s,s)+Cu(s,s)+Fe_2Ti+NiTi+Cu_3Ti(zoneⅡ)/Ag(s,s)+Cu(s,s)+Cu_2Ti+Al(s,s)+TiC+TiO(zoneⅢ)/Al_2O_3.Themaximumshearstrengthof139MPawasmeasuredforas-brazedAl_2O_3/Invarjointbrazedat850℃for25minor900℃for15min.
简介:Dynamicsinpartialtransientliquidphasebonding(PTLPbonding)ofSi3N4ceramicwithTi/Cu/Timulti-interlayerwassystematicallystudiedthroughmicro-analysisofjointinterfaces.Theresultsshowthatgrowthofreactionlayerandisothermalsolidificationprocessiondoatthesametime.GrowthofreactionlayerandmovingofisothermalsolidificationinterfaceobeytheparaboliclawgovernedbythediffusionofparticipatingelementsduringthePTLPbonding.Coordinationoftheabovetwodynamicsprocessisdonethroughtimeandtemperature.Whenreactionlayerthicknessissuitableandisothermalsolidificationprocessisfinished,thehighbondingstrengthatroomtemperatureandhightemperatureareobtained.
简介:Anewhardfacingprocess,reactivebrazecoatingprocess(RBCC)wasstudied,and(TiC+Cr3C2)/FecompositecoatingswerepreparedbyRBCCusingcarbon,Cr3C2,iron,ferrochromiumandtitaniumpowderastherawmaterialsinvacuumbrazefurnace.TheresultsshowthatTiCisin-situsynthesizedinthecoatings.ThemethodsofintroducingCr3C2havegreateffectsonthedistributionofTiC.AddingCr3C2directlytotherawmaterialsforcoatings,fineTiCparticlesaggregateintodiscoidsparalleltothecoatingsurface,whereas,in-situsynthesizingCr3C2incoatings,theaggregationsofTiCarelumpish.Duringbrazecoating,Cr3C2particlesdirectlyaddeddissolveandprecipitatetobecomeneedle-shaped.Thecoatingshaveanevenandsmoothsurfaceandarecombinedwiththeirmildsteelsubstratesbyametallurgicalbonding.
简介:TheHAZmicrostructureandperformanceofQuenchingandTemperingmodetemperbeadweldingandgeneralweldedjointswhichweremadeonSA508-3steelof60mmthicknesswerecomparedinthisarticle.Theresultshowsthattemperingsorbitewhichhasexcellentoverallperformancewasobtainedinbothmodes.ThemicrostructureofQuenchingandTemperingmodeweldedjointsgotmorefinegrain.Eventhoughthehardnessoftemperingbeadweldedjointsishigherthanthegeneralone,itstillmeetsthestandardswhichislowerthan350HV.TheimpactabsorbingenergyofeachdistrictoftemperingbeadweldedjointsHAZreached170J,whichisequaltogeneralone.
简介:ThediffusionbondingofAZ3\BMgalloyandQ235steelwasinvestigatedwithaZn-5AIalloyasinterlayerandunderdifferentholdingtimerangingfrom3to1200s.Themicrostructureandphasecompositionsofbondedjointswerecharacterizedbyscanningelectronmicroscopy(SEM),energydispersivespectrometer(EDS)andX-raydiffraction(XRD)methods.TheshearstrengthofMgalloy/steeljointswasmeasuredbytensiletester.Itwasfoundthatthemicrostructureofbondedjointsevolveddramaticallyalongwiththeprolongationofholdingtime.Undertheholdingtimeof3s,themainpartofjointwascomposedofMgZn2phaseanddispersedAl-richsolidsolutionparticles.Whenincreasedtheholdingtimemorethan60s,theexcessivesolutionofAZ3\Bintotheinterfacialreactionarealedtotheformationofcoarsephaseandeutecticmicrostructure,andalsothecomplexFe-AlandMg-Al-ZnIMCsattransitionlayerclosedtoQ235steelside.Accordingtothetensiletestingcharacterizations,thejointsobtainedunderholdingtimeof3sexhibitedthebestshearstrengthof84MPa,andthefractureoccurredattheintermediarypartofjointwheretheflexibleAl-richsolidsolutionparticlescouldhelptoimpedethemicrocrackpropagations.Withprolongingtheholdingtimeto600s,theshearstrengthofjointswasdeterioratedenormouslyandthefracturepositionwasshiftedtothetransitionlayerpartclosedtoQ235steel.
简介:Fe3AlandCr18-Ni8steelwerebondedinvacuumandaninterfacewasformedbetweenFe3AlandCr18-Ni8steel.Stressdistributionatthediffusion-bondedinterfacewasresearchedbynumericalsimulationandfiniteelementmethod(FEM).TheresultsindicatedthatthepeakstressappearedattheinterfacenearCr18-Ni8steelside.Thisisthekeyfactortoinducecrackatthisposition.Withtheenhancementofheatingtemperature,thepeakstressatthebondedinterfaceincreases.Whenthetemperatureis1100℃,thepeakstressisupto65.9MPa,whichisbiggerthanthatat1000℃by9.4%.Inaddition,thepeakstressbecomesbiggerwiththeincreaseofthethicknessofbasemetalfrom1mmto8mm.Whilethethicknessismorethan8mm,thepeakstressvariesslightlywiththechangeofthethickness.
简介:ThedistributionsoftheaxialstressandshearstressinAl2O3-TiC/Q235diffusionbondedjointswerestudiedusingfiniteelementmethod(FEM).Theeffectofinterlayerthicknessontheaxialstressandshearstresswasalsoinvestigated.Theresultsindicatethatthegradientsoftheaxialstressandshearstressaregreatnearthejointedge.ThemaximalshearstressproducesattheinterfaceoftheAl2O3-TiCandTiinterlayer.WiththeincreaseofCuinterlayerthickness,themagnitudesoftheaxialstressandshearstressfirstdecreaseandthenincrease.Thedistributionoftheaxialstresschangesgreatlywithalittlechangeintheshearstress.TheshearfractureinitiatesattheinterfaceoftheAl2O3-TiC/TiinterlayerwithhighshearstressandthenpropagatestotheAl2O3-TiCside,whichisconsistentwiththestressFEMcalculatingresults.