简介:Thestatusandthevariationofelectricalresistanceofimpactedcarbonfiber/epoxy-matrixcompositeswerestudiedbyultrasonicF-scanandelectricalresistancemeasurementTheexperimentalresultsshowsthatimpactdamageenergythresholdvalueofcarbonfabric/epoxy-matrixcompositescandeterminebyusingultrasonicF-scan.Whentheimpactenergyexceedsthethresholdvalue,damageisgeneratedincomposites.Electricalresistanceofimpactedcompositesischangedowingtothecontactofeachcarbonfiberunitincomposites,whichcauseachangeoftheseries-parallelinconductors.Theveracityofdetectingimpactdamageincompositescanbeimprovedinthiscase.