简介:SomenewNi-saving25Crduplexstainlesssteels(DSS)havebeendeveloped.Theresultsindicatethatthealloyhasabalancedferrite-austeniterelationafterhotforgeandsolidsolutiontreatmentat1000℃.TheelementsWandCuhaveamarkedeffectonthemicrostructureofthealloy.ThepittingpotentialofthesteeladdingWandCuelementsreachesthemaximumvalueof435mV.Thetensilestrengthandpercentageofareareductionofallsteelsinthispaperare800-900MPaand60%-70%,respectively.Thetensileelongationsofthealloysareallabove30%.Theexperimentalsteelshavegoodcorrosionandmechanicalproperty.
简介:Usingmetallographicobservationandmechanicalmeasurement,themicrostructureandmechanicalpropertiesofGH4169Galloyhasbeeninvestigated.Theeffectofthephosphorus,borontraceelementsonmechanicalpropertiesoftheGH4169Galloyarecomparedandanalyzed.Theresultsshowedthatthehot-workabilityoftheGH4169Galloyisverygood.ThestressrupturespropertiesofGH4169Galloyisover3timesthanthetraditionalGH4169alloy.
简介:Improvingtheunitheatefficiency,reducingcoalconsumptionandtheemissionofCO2andmeetingtherequirementsofenvironmentalprotectionandenergyconservationisthegoaloftheboilerandthepowerindustry.Developmentsoflargecapacityandhighparameterultra-supercritical(USC)unitsarethetendencyofthepowerindustry.ThereisnodoubtthatthedevelopmentofUSCunitsisbasedonthedevelopmentofmaterials,especiallythematerialsusedforsuper-heaterandreheaterinhigh-temperatureUSCboiler.Duetothelongtimeexposuretotheharshenvironment,suchasbearingthe600℃steamoxidation,andwithstandingthecorrosivefluegasandflyasherosion,thematerialsrequirenotonlygoodhigh-temperaturestrength,butalsoagoodcorrosionresistance.Inconsiderationoftherequirementscitedabove,foreigncountrieshaddevelopedTP310HCbN(07Cr25Ni21CbN)austeniticheat-resistantsteel.However,thedomesticdemandsforthismaterialstilldependonimportandthecostishigh,sotheboilerandthepowerindustryexpectseagerlythatthesesteelscanbeproducedbydomesticmetallurgicalindustry,especiallyBaosteel,toreplacetheimportedproducts.Inordertosatisfytherequirementsofdomesticmanufacturingsuper-heaterandreheaterusedinultra-supercriticalpowerboiler,afterdevelopedT23、T91、T92、S30432highpressureboilertube,BaosteelbegantodevelopTP310HCbN(07Cr25Ni21CbN)austeniticstainlesssteeltubeinJanuaryof2007.Thisstudydescribesthecompositiondesign,themanufacturingprocessofproduct,andtheassessmentofperformanceofBaosteel’sTP310HCbN(07Cr25Ni21CbN).ThedataindicatesthatpropertiesofBaosteel’sTP310HCbN(07Cr25Ni21CbN)conformtotheASMESA-213standardandGB5310standard,soitcansubstitutetheimportedproductsandissuitableformanufacturingpowerstationboilerofgreatcapacityandhighsteamparameters.