简介：Ni-W-P-CeO2-SiO2nano-compositecoatingswerepreparedonthecarbonsteelsurfacebypulseco-depositionofnickel,tungsten,phosphorus,nano-CeO2andnano-SiO2particles.Theinfluenceofnano-SiO2particlesconcentrationsinelectrolyteonmicrostructuresandpropertiesofthenano-compositecoatingswereresearched,andthecharacteristicswereassessedbychemicalcompositions,elementdistribution,depositionrate,microhardnessandmicrostructures.Theresultsindicatethatwhennano-SiO2particlesconcentrationsinelectrolytearecontrolledat20g·L-1,thedepositionratewith27.07μm·h-1andthemicrohardnesswith666Hvofthenano-compositecoatingsarehighest,elementlinescanningandareascanninganalysesshowthattheaveragecontentsofelementsW,P,SiandCeinthenano-compositecoatingsareclose,displayingthatthedistributionofeveryelementwithinthenano-compositecoatingsiseven.Anincreaseinnano-SiO2particlesconcentrationsinelectrolyte(whenlowerthan20g·L-1)leadstorefinementingrainstructureofnano-compositecoatings,butwhenitimprovedto30g·L-1,thecrystallitesizesincreaseagainandinthemeantimetherearealotofsmallbosswithnodulationshapeappearingonthesurfaceofnano-compositecoatings.

简介：Theaimofthisresearchistopulseco-depositnano-CeO2particlesintoNi-W-Balloycoatingsinordertoimprovethesurfaceproperties.Theinfluenceofpulsefrequencyanddutycircleondepositionrate,microhardnessandmicrostructures,andtheinfluenceofheattreatmenttemperatureonphasestructures,microhardnessandabrasivityofNi-W-B-CeO2compositecoatingswereinvestigated.Theresultsindicatedthatthepulseco-depositionofnickel,tungsten,boronandnano-CeO2particlefromthebathwhichnano-CeO2particlewassuspendedbyhighspeedmechanicalstirringledtotheNi-W-B-CeO2compositecoatings,possessingbettermicrohardnessandabrasionresistancewhenheat-treatedat400℃for1h.Themicrohardnessas-depositedwith636Hzandthedepositionratewith0.0281mm·h-1wasthehighestatpulsefrequencywith1000Hzandpulsedutycirclewith10%.Microstructuresanalysisdisplaysthatdecreasingpulsedutycycleleadstorefinementingrainstructuresandtheimprovementofmicrostructures.X-raydiffractionshowsthatthecompositecoatingas-depositedwasmainlyintheamorphousstateandpartiallycrystallized,butwhenheattreatedat400℃,thecrystallizationtrendwasstrengthenedfurther.