Theeffectsoftwopost-weldheattreatmentprocessesonthemicrostructureandfatiguepropertiesoftheelectronbeamweldedjointsof30CrMnSiNi2Asteelwerestudied.Electronbeamlocalpost-weldheattreatment(EBLPWHT),inavacuumchamber,immediatelyafterweldingandatraditionalfurnacewholepost-weldheattreatment(FWPWHT)wereaccepted.Theexperimentalresultsshowthat,afterEBLPWHT,themainmicrostructureofweldischangedfromcoarseacicularmartensiteintolathmartensite,andbasemetalischangedfromferriteandperliteintoupperbainiteandresidualaustenite,howeverthemicrostructuresofdifferentzonesofjointsinFWPWHTconditionsaretemperedsorbite.Thefatiguecrackgrowthrateda/dNofweldsandbasemetalarenotobviouslychangedamongEBLPWHT,FWPWHTtestandas-welded(AW)test,asthemechanicalpropertiesofmaterialshaveacertainbutnotlargeeffectontheda/dNofweldedjoints.TheresistancetonearthresholdfatiguecrackgrowthdataofweldedjointscanbelargelyimprovedbyEBLPWHTanditisrelatedtomicrostructureandcrackclosureeffect.