简介：LayeredcathodematerialLiCo1/3Ni1/3Mn1/3O2wassynthesizedbyPechiniprocess,andinvestigatedusingX-raydiffraction(XRD),scanningelectronmicroscopy(SEM)andgalvanostaticcharge/dischargecycling.Thesampleiswell-crystallizedandhasaphase-purea-NaFeO2structure.Theparticlesizesareuniform,anddistributedintherangeof20-200nm.TheinitialdischargecapacityoftheLi/LiCo1/3Ni1/3Mn1/3O2cellwasabout149mAh·g-1whenitwascycledatavoltagerangeof4.5-2.3Vwithaspecificcurrentof0.25mA.Theresultisbetterincomparisonwithsolid-statesolutionmethod.Thesyntheticprocedurewasdiscussed.Threemajorreactions:chelation,esterification,andpolymerizationsuccessivelyoccurred.

简介：EmployingLi2CO3,NiO,Co3O4,andMnCO3powdersasstartingmaterials,Li[Ni1/3Co1/3Mn1/3]O2wassynthesizedbysolid-statereactionmethod.Variousgrindingaidswereappliedduringmillinginordertooptimizethesynthesisprocess.Aftersuccessiveheattreatmentsat650and950℃,thepreparedpowderswerecharacterizedbyX-raydiffraction(XRD)analysis,scanningelectronmicroscopy,andtransmissionelectronmicroscopy.Thepowderspreparedbyaddingsalt(NaCl)asgrindingaidexhibitaclearR3mlayerstructure.ThepowdersbyothergrindingaidslikeheptaneshowsomeimpuritypeaksintheXRDpattern.Theformerpowdersshowauniformparticlesizedistributionoflessthan1μmaveragesizewhilethelattershowsawidedistributionrangingfrom1to10μm.EnergydispersiveX-ray(EDX)analysissshowthattheratioofNi,Co,andMncontentinthepowderisapproximately1/3,1/3,and1/3,respecively.TheEDXdataindicatenoincorporationofsodiumorchlorineintothepowders.Charge-dischargetestsgaveaninitialdischargecapacityof160mAh·g-1forthepowderswithNaCladditionwhile70mAh·g-1forthepowderswithheptane.

简介：PolycrystallinesamplesofLa12x(Sr12yAgy)xMnO3(y=0.0,0.2,0.4,0.6,1.0)werepreparedbythesolid-statereactionmethod.ThetemperaturestabilityofmagnetoresistanceandmagnetoresistanceenhancementinLa1-x(Sr1-yAgy)xMnO3systemwithbothunivalentandbivalentelementsdopedatAsiteandwithunchangedvalueofMn3+/Mn4+ratiowereexploredthroughthemeasurementsofX-raydiffractionpatterns,magnetiza-tion-temperature(M-T)curves,resistivity-temperature(q-T)curvesandmagnetoresistance-temperature(MR-T)curves.Theresultsareasfollows:therearetwopeaksintheq-TcurvesofthesampleswithAgdoping,oneiscausedbyresistancechangeduringtheparamagnetism-ferromagnetismtransition,andtheotherisfromboundary-dependentscatteringofconductionelectronsontheboundariesofgrains.ThepeakvalueofMRincreaseswithincreasingAgdopingcontent,anditincreasesfrom8.2%fory=0.2to29.6%fory=1.0underthemagneticfieldofB=0.8T;MRremainsaconstantof12%inthetemperaturerangeof218-168Kforthesamplewithy=1.0,andthetemperaturestabilityofMRisinfavorofthepracticalapplicationofMR.

简介：晶体结构和加氢行为(La_(1-x)Mg_x)_3Al(x=0.1，0.2，0.3，和0.4)合金被调查。这被发现有x=的合金0.1La和第0.2consi(Mg，艾尔)，La，和一个新奇阶段。新奇阶段作为La_2Al被决定。当Mg满足增加，La_2Al的数量减少，这被显示出。当x增加到0.3时，onlyLa(Mg，艾尔)并且La_2Al的小数量存在。当x是0.4时，La_2Al阶段消失，合金包含两La(Mg，艾尔)并且La(艾尔，Mg)_2洗阶段。(La_(0.9)Mg_(0.1))_3Al并且(La_(0.7)Mg_(0.3))_3Al合金能被氢的吸收在473K分解成LaH_3，MgH_2，和La_2Al_5。

简介：招金矿业股份有限公司河东金矿坚持走科技探矿之路，不断加大探矿增储和矿产资源综合开发利用的科技投入力度，《杨家-白石夼地区金矿地球物理找矿研究》和《山东招远河东金矿成矿系统研究及找矿预测》两个探矿科研项目，取得了理想的探矿效果，1—3季度探矿新增金属量1532公斤，不仅实现了储量平衡，延长了矿山服务年限，而且为实现规模经营、保证矿山可持续发展奠定了坚实的基础。

简介：GaxIn1-xAs1-ySbyalloyshavebeengrownbyatmosphericpressureMOCVDonn-GaSb（Te-doped）substrate.Thesohdcompositionwasdeterminedbyusingelectronmicroprobe.ThealloysofGalnAsSbwithcompositioninmiscibilitygapweresuccessfullygrown.TheopticalpropertiesofGaxIn1-xAs1-ySbylaverswerecharacterizedbythephotoluminescenceandtheinfraredabsorption.Thespectralresponsesofp+-GaInAsSb/p-GaxIn1-xAs1-ySby/n-GaSbdetectorsshowedwavelengthcutoffat2.4μmanddetectivity-D*=5×108cmHz1/2/Watroomtemperature.

简介：Thecorrosionfatiguebehaviorofepoxy-coatedMg–3Al–1Znalloywasinvestigatedinairand3.5wt%NaClsolution.Epoxycoatingasanewmethodwasusedtoimprovethecorrosionfatiguepropertyofthematerial.Resultsshowthatthefatiguelimit(FL)ofthecoatedspecimensishigherthanthatoftheuncoatedspecimensin3.5wt%NaClsolutionbecauseofthestrengtheningandblockingfunctionsoftheepoxycoating.TheFLofthecoatedspecimensin3.5wt%NaClsolutionisashighasthatinair.Itimpliesthatthecoatedspecimensarenotassensitivetotheenvironmentasthemagnesiumalloy.Thelowtensilestrengthandtheshortelongationofthepureepoxycoatingleadtothatthefatiguecrackofthecoatedspecimenisalwaysinitiatedfromtheepoxy-coatingfilmPoresandpinholesacceleratethefatiguecrackinitiationprocess.PinholesarecausedbythecorrosionreactionsbetweentheepoxycoatingandtheNaClsolution.

简介：前言3D打印技术，又称增材制造技术，以前称快速成型“快速成形”技术，出现在上世纪80年代中后期。世界上（包括国内）的第一次研究开发热度期，在上世纪80年代中后期至2003年左右。2003年至2012年出现了研究开发的低谷，其原因是多方面的。自从2012年开始，该技术的研究开发及应用又有了新的转机，其原因众所周知，因此，自2012年以来，3D打印技术出现了新一轮的研究开发热度期，并且，其热度远远大于第一次的热度。

简介：ThermodynamicmodelsofcalculatingmassactionconcentrationsforstructuralunitsorioncouplesinRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionsweredevelopedbasedontheionandmoleculecoexistencetheoryat298.15K.Atransformationcoefficientisneededtocomparethecalculatedmassactionconcentrationandthereportedactivitybecausetheyareobtainedatdifferentstandardstatesandconcentrationunits.TheresultsshowthatthetransformationcoefficientsbetweenthecalculatedmassactionconcentrationsandthereportedactivitiesofthesamestructuralunitsorioncouplesinRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionschangeinaverynarrowrange.ThetransformedmassactionconcentrationsofstructuralunitsorioncouplesinRbCl-H2Obinarysystemareingoodagreementwiththereportedactivities.ThetransformedmassactionconcentrationsofRbClandRbNO3inRbCl-RbNO3-H2Oternarysolutionarealsoingoodagreementwiththereportedactivities,aRbCland3RbNOa,withdifferenttotalionicstrengthsas0.01,0.05,0.1,0.5,1.0,1.5,2.0,3.0and3.5mol/kg,respectively.AllthoseresultsmeanthedevelopedthermodynamicmodelofstrongelectrolyteaqueoussolutionscanreflectstructuralcharacteristicsofRbCl-H2ObinaryandRbCl-RbNO3-H2Oternarystrongelectrolyteaqueoussolutionsandthemassactionconcentrationalsostrictlyfollowsthemassactionlaw.

简介：1．价格走势分析1．1国际铂价受日本地震影响大幅下跌2010年，由于需求改善，铂价震荡上行，年末上涨至1750美元／盎司。2011年初，铂价承接去年的上涨趋势，1月中旬在投资者推动下上涨至1800美元／盎司，随后铂价出现小幅回调。2月初，受南非供应吃紧影响铂再次发力，快速突破1850美元阻力，2月9日最高达到1864．5美元／盎司。

简介：针对激光直接沉积修复的1Cr15Ni4Mo3N钢零件在磁粉检测时出现的磁痕现象,采用接触通电、湿磁粉连续法,对设计的试样进行磁粉检测,确定磁痕显示位置;利用光学显微镜对磁痕显示处形貌及修复接头和组织进行观察和研究,分析磁痕的性质和形成原因。研究发现:激光直接沉积修复1Cr15Ni4Mo3N钢在磁粉检测过程中与修复区外轮廓完全重合的磁痕显示是伪磁痕显示,主要是由修复区与基体中奥氏体含量的差异造成的。

简介：本文将介绍新研制的一种用于人造金刚石合成的触媒合金JX－1，其合成效果明显优于Ni70Mn25Co5，且金刚石的颜色呈金黄色，金刚石的TI、TTI值较高，磁化率较低。

简介：转子工作时不仅需要承受高速旋转（3000r／min）所产生的巨大离心力，同时还承受扭转和弯曲的应力．是汽轮机上重要的安全部件。因此，要求其强度高、韧性好、组织性能均匀、残余应力小等，探伤执行标准为JB／T1265-2002。转子的锻造难度大干一般轴类锻件．因此必须要有可靠的工艺、先进的设备和熟练的操作工人才能保证锻出优质的转子。

简介：双面挠性覆铜板及其制作方法／CN101420820／申请人广东生益科技股份有限公司本发明涉及一种双面挠性覆铜板及其制作方法，该双面挠性覆铜板包括一单面覆铜板、涂布于该单面覆铜板上的胶粘剂层、以及压覆于该胶粘剂层上的另一铜箔或另一单面挠性覆铜板，所述单面覆铜板包括一铜箔以及涂布于铜箔上的聚酰亚胺层，所述聚酰亚胺层与胶粘剂层相邻设置。

简介：本文主要介绍在PowerMILL创建刀具路径之前所需要的初始设置：定义毛坯、定义切削刀具、设置进给率等。

简介：前言：环境中的铅作为一种污染物，对人身体有重大危害，在全世界范围内不存在争议。现在ROHS法案即将正式实施，这标志着无铅化时代已经来临。日本是世界工业强国，为了提高竞争门槛，领先于竞争对手，现在已经制定了无卤覆铜板标准。日本企业积极行动，在国内全部采用无卤材料来生产覆铜板。本文介绍了一种同时满足无卤阻燃和适应无铅焊接的FR-1的研制工作。

简介：1Cr15Ni4Mo3N沉淀硬化不锈钢螺栓零件在制造工序磁粉检测时，发现螺栓表面有一条疑似裂纹状线性磁痕显示，后采用荧光渗透检测方法进行辅助检测，原磁痕显示处未见异常荧光显示。结合金相试验分析发现，螺栓原材料内呈带状分布的残余奥氏体，破坏了基体组织和材料磁性的连续性导致出现磁痕显示。研究为该材料在零件制造中磁粉检测的磁痕判定提供了依据。

简介：通过油井套管穿孔实例对其穿孔种类和原因进行了较为全面的分析，同时提出了预防治理的具体措施。

简介：室温下用溶胶凝胶自蔓延燃烧法合成平均尺寸约50nm的仿立方体结构KxNa1-xNbO3纳米粉体并制备成陶瓷,对陶瓷进行相结构、显微组织以及电性能的表征。XRD结果表明,KxNa1-xNbO3陶瓷为纯的钙钛矿结构,且K0.5Na0.5NbO3陶瓷具有正交相和单斜相的混合相结构。SEM结果表明,所有陶瓷样品均为孪晶分布,且孪晶分布中小晶粒数随K+含量的增加而减少。在室温下,晶粒尺寸均匀且具有最大密度的K0.5Na0.5NbO3陶瓷具有较优异的电性能:εr=467.40,tanδ=0.020,d33=128pC/N,kp=0.32。K0.5Na0.5NbO3陶瓷的优良电性能说明溶胶凝胶自蔓延燃烧法合成的K0.50Na0.50NbO3粉体性能较好,且制备的陶瓷满足无铅压电材料应用。

简介：福建省经济贸易委员会于2010年11月2日组织召开了由福建畅联电子有限公司研制开发的“PS-3多路恒电位仪”、“HPS-1高频开关恒电位仪”新产品及科技成果鉴定会。由中石油、中石化管道防腐蚀专家为主的鉴定委员会一致认为：上述产品设计新颖、合理，技术指标先进，整体技术达到国内领先水平。